Grade for rotomolding. Available color: natural. Light and heat stabilized. Mold-release agent.
Easy to be processed in the same conditions as polyethylene. High thermal and chemical resistance. Outstanding mechanical properties. Low permeability to gas and hydrocarbon.
Example applications: Oil tank, hydraulic fluid tank.
ISO data provided by the manufacturer, Arkema.
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(屈服) | MPa | psi | 50 mm/min |
| 伸长率 (断裂) | Nominal Strain; 50 mm/min | ||
| 屈服伸长率 | 50 mm/min | ||
| 拉伸模量 | GPa | ksi | 1 mm/min |
| 简支梁无缺口冲击强度 | |||
| Low Temp | |||
| 简支梁缺口冲击强度 | J/cm² | ft-lb/in² | |
| J/cm² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 电阻率 | ohm-cm | ohm-cm | |
| 表面电阻 | ohm | ohm | |
| 介电强度 | kV/mm | kV/in | |
| 相比耐漏电起痕指数(CTI) | V | V |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | µm/m-°C @Temperature 20.0 °C | µin/in-°F @Temperature 68.0 °F | |
| 载荷下热变形温度(0.46 MPa) | °C | °F | |
| 载荷下热变形温度(1.8 MPa) | °C | °F | |
| 维卡软化温度 | °C | °F | 50°C/hr; 50N |