| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|
| 剥离强度 | kN/m | pli | LD Polyethylene, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330 |
| | kN/m | pli | LD Polyethylene, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330 |
| | kN/m | pli | Polycarbonate 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330 |
| | kN/m | pli | LD Polyethylene, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| | kN/m | pli | HD Polyethylene, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| | kN/m | pli | HD Polyethylene, 90° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| | kN/m | pli | HD Polyethylene, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330 |
| | kN/m | pli | Polycarbonate 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330 |
| | kN/m | pli | LD Polyethylene, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| | kN/m | pli | LD Polyethylene, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| | kN/m | pli | HD Polyethylene, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| | kN/m | pli | LD Polyethylene, 90° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| | kN/m | pli | HD Polyethylene, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| | kN/m | pli | LD Polyethylene, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| | kN/m | pli | Polypropylene, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| | kN/m | pli | Polypropylene, 90° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| | kN/m | pli | HD Polyethylene, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330 |
| | kN/m | pli | HD Polyethylene, 180° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| | kN/m | pli | Stainless Steel, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| | kN/m | pli | Glass, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| | kN/m | pli | LD Polyethylene, 180° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| | kN/m | pli | Polypropylene, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330 |
| | kN/m | pli | Polycarbonate 90° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| | kN/m | pli | Polypropylene, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| | kN/m | pli | Glass, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| | kN/m | pli | HD Polyethylene, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| | kN/m | pli | Stainless Steel, 90° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| | kN/m | pli | Polycarbonate 90° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| | kN/m | pli | Glass, 90° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| | kN/m | pli | Stainless Steel, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330 |
| | kN/m | pli | Glass, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330 |
| | kN/m | pli | Polypropylene, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| | kN/m | pli | Stainless Steel, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| | kN/m | pli | Polypropylene, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330 |
| | kN/m | pli | Polycarbonate 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| | kN/m | pli | Stainless Steel, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| | kN/m | pli | Polypropylene, 180° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| | kN/m | pli | Polycarbonate 180° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| | kN/m | pli | Glass, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| | kN/m | pli | Polycarbonate 180° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| | kN/m | pli | Polypropylene, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| | kN/m | pli | Glass, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| | kN/m | pli | Stainless Steel, 180° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| | kN/m | pli | Stainless Steel, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| | kN/m | pli | Stainless Steel, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330 |
| | kN/m | pli | Glass, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330 |
| | kN/m | pli | Glass, 180° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| | kN/m | pli | Polycarbonate 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |