Celanese FORTRON® 4332D4 Mineral and Glass Reinforced Polyphenylene Sulfide (PPS)

Description: Fortron 4332D4 offers a unique balance of properties based on a high mineral and glass reinforced composition, complementing our other 6165 product offerings. The heat resistance under load bearing conditions is excellent for this product. As with all Fortron grades this product is inherently flame-retardant. Applications include electronic and industrial components.

Information provided by Celanese Corporation.

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	g/cc	lb/in³	ISO 1183
饱和吸水率			ISO 62

机械性能	额定值 (公制)	额定值 (英制)	测试方法
抗张强度(断裂)	MPa	psi	5 mm/min; ISO 527-2/1A
伸长率 (断裂)			5 mm/min; ISO 527-2/1A
拉伸模量	GPa	ksi	1 mm/min; ISO 527-2/1A
弯曲强度	MPa	psi	ISO 178
弯曲模量	GPa	ksi	ISO 178
悬壁梁缺口冲击强度	kJ/m²	ft-lb/in²	ISO 180/1A

热性能	额定值 (公制)	额定值 (英制)	测试方法
熔融温度	°C	°F	ISO 11357-1,2,3
载荷下热变形温度(1.8 MPa)	°C	°F	ISO 75-1, -2
载荷下热变形温度(8.0 MPa)	°C	°F	ISO 75-1, -2
玻璃化转变温度，Tg	°C	°F	ISO 11357-1,-2,-3

加工性能	额定值 (公制)	额定值 (英制)	测试方法
加工（熔体）温度	°C	°F
模具温度	°C	°F
干燥温度	°C	°F
干燥时间	hour	hour