Multibase Multi-Flex® TPE A 5801 LC BLK

Multi-Flex® LC compounds are a new generation elastomers exhibiting improved compression set at elevated temperature. Multi-Flex® TPE compounds are based on Shell's Kraton G technology and feature excellent heat and ozone resistance. LC products cover a wide temperature span from -40°F to 300°F. Multi-Flex TPE contains Kraton™ G.

Data provided by Multibase.

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	g/cc	lb/in³	ASTM D792
熔体流动速率	g/10 min @Load 5.00 kg, Temperature 230 °C	g/10 min @Load 11.0 lb, Temperature 446 °F	ASTM D-1238

机械性能	额定值 (公制)	额定值 (英制)	测试方法
肖氏硬度 (邵氏 A)			10 sec; ASTM D-2240
极限抗拉强度	MPa	psi	ASTM D638
伸长率 (断裂)			ASTM D638
100% 模量	GPa	ksi	ASTM D638
300％模量	GPa	ksi	ASTM D638
撕裂强度	kN/m	pli	ASTM D624
永久压缩			for 70 hours at 23°C; ASTM 395
	@Temperature 70.0 °C	@Temperature 158 °F	for 70 hours at 70°C; ASTM 395
	@Temperature 100 °C	@Temperature 212 °F	70 hours at 100°C; ASTM 395