Rigid grade with glass fiber filler (15%) for injection molding.
Available color: natural. Light and heat stabilized. Mold-release agent.
Rigidity combined with good impact strength. High compressive strength. Very low shrinkage: include 0,5% on average for the design of the mold. Low coefficient of linear expansion. High dimensional stability.
Example applications: Mechanical fittings.
ISO data provided by the manufacturer, Arkema.
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 熔体流动速率 | g/10 min @Load 2.16 kg, Temperature 235 °C | g/10 min @Load 4.76 lb, Temperature 455 °F |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 极限抗拉强度 | MPa | psi | 5 mm/min |
| 伸长率 (断裂) | 5 mm/min | ||
| 拉伸模量 | GPa | ksi | 1 mm/min |
| 简支梁无缺口冲击强度 | J/cm² | ft-lb/in² | |
| J/cm² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | ||
| 简支梁缺口冲击强度 | J/cm² | ft-lb/in² | |
| J/cm² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 维卡软化温度 | °C | °F | 50°C/hr; 50N |