High-strength and stiff parts; low coefficient of expansion.
dynamic stress
Electrically conductive, suitable for continuous discharging of statically generated electricity.
Handles, levers, rollers, extrusion profiles.
Information provided by Lehmann & Voss & Co.KG| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | g/cc | g/cc | ISO 1183 |
| 吸水率 | 23°C/24h | ||
| 线性成型收缩率 | cm/cm | in/in |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度 | MPa | psi | |
| 屈服伸长率 | |||
| flexural | |||
| 弹性模量 | GPa | ksi | |
| 弯曲强度 | MPa | psi | |
| 弯曲模量 | GPa | ksi | |
| 简支梁无缺口冲击强度 | J/cm² | ft-lb/in² | flatwise; ISO 179 1fU |
| J/cm² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | ISO 179 | |
| 简支梁缺口冲击强度 | J/cm² | ft-lb/in² | ISO 179 1eA |
| J/cm² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | ISO 179 eA | |
| 动态摩擦系数 | |||
| 静态摩擦系数 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 表面电阻 | <= ohm | <= ohm | |
| 绝缘电阻 | <= ohm | <= ohm |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线性热膨胀系数 | µm/m-°C | µin/in-°F | DIN 53752 |
| 导热系数 | W/m-K | BTU-in/hr-ft²-°F | DIN 52612 |
| 最高工作温度, Air | °C | °F | |
| °C | °F | short term | |
| 载荷下热变形温度(1.8 MPa) | °C | °F | |
| 维卡软化温度 | °C | °F | DIN ISO 306 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工温度 | °C | °F | mass temp |
| 射嘴温度 | °C | °F | |
| 1区 | °C | °F | |
| 2区 | °C | °F | |
| 3区 | °C | °F | |
| 模具温度 | °C | °F | |
| 干燥温度 | °C @Time 36000 - 57600 sec | °F @Time 10.0 - 16.0 hour | Dehumidifying dryer |
| °C @Time 14400 - 21600 sec | °F @Time 4.00 - 6.00 hour | or |
| 材料描述 | 测试方法 | |
|---|---|---|
| 颜色 | natural color (black) |