Characteristics:
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | g/cc | g/cc | ASTM D792 |
| 水分吸收 | @Time 86400 sec | @Time 24.0 hour | ASTM D570 |
| 粘度测量 | [dl/gr] Intrinsic; ASTM D2857 | ||
| 线性成型收缩率 | cm/cm @Thickness 1.60 mm | in/in @Thickness 0.0630 in | ASTM D955 |
| 熔体流动速率 | g/10 min @Load 2.16 kg, Temperature 235 °C | g/10 min @Load 4.76 lb, Temperature 455 °F | ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（M 级） | ASTM D785 | ||
| 抗张强度 | MPa | psi | ASTM D638 |
| 伸长率 (断裂) | ASTM D638 | ||
| 弯曲强度 | MPa | psi | ASTM D790 |
| 弯曲模量 | GPa | ksi | ASTM D790 |
| 悬壁梁缺口冲击强度 | >= J/cm @Thickness 6.35 mm | >= ft-lb/in @Thickness 0.250 in | ASTM D256 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | >= ohm-cm | >= ohm-cm | ASTM D257 |
| 表面电阻 | >= ohm | >= ohm | ASTM D257 |
| 介电常数 | @Frequency 60.0 Hz | @Frequency 60.0 Hz | ASTM D150 |
| 介电强度 | >= kV/mm @Thickness 2.00 mm | >= kV/in @Thickness 0.0787 in | ASTM D149 |
| 耗散因数 | @Frequency 60.0 Hz | @Frequency 60.0 Hz | ASTM D150 |
| 耐电弧性 | sec | sec | ASTM D495 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线性热膨胀系数 | µm/m-°C | µin/in-°F | ASTM D696 |
| 熔融温度 | °C | °F | DSC |
| 载荷下热变形温度(0.46 MPa) | °C | °F | ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | °C | °F | ASTM D648 |
| 可燃性(UL94) | @Thickness 1.60 mm | @Thickness 0.0630 in |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工温度 | °C | °F | |
| 射嘴温度 | °C | °F | |
| 模具温度 | °C | °F | suitable temperature 40-60°C |
| 注射压力 | MPa | psi | |
| 保压 | MPa | psi | |
| 背压 | MPa | psi | |
| 螺杆转速 | rpm | rpm | to be chosen in such a way that plasticizing time is just within cooling time |
| 材料描述 | 测试方法 | |
|---|---|---|
| Carboxyl End Groups | <30 meq/kg | Chang Chun |
| 颜色 | <2 | b |
| >85 | L, Chang Chun | |
| 注射速率 | middle |