Features: Good Wear Resistance; Low Friction
Additional Properties: Wear Rate - ASTM D3702 5.00E-5 m/hr
Automotive Specifications PSA Peugeot-Citroën SPA X62 5102
Information provided by Solvay Specialty Polymers.| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | ASTM D792 |
| 填料含量 | Glass Fiber | ||
| 吸水率 | @Time 86400 sec | @Time 24.0 hour | ISO 62 |
| 线性成型收缩率,Flow | cm/cm @Thickness 3.18 mm | in/in @Thickness 0.125 in | |
| 线性成型收缩率，横向 | cm/cm @Thickness 3.20 mm | in/in @Thickness 0.126 in | ASTM D955 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（M 级） | ASTM D785 | ||
| 洛氏硬度（R 级） | ASTM D785 | ||
| 抗张强度 | MPa | psi | ASTM D638 |
| MPa | psi | ISO 527-2 | |
| 伸长率 (断裂) | ISO 527-2 | ||
| ASTM D638 | |||
| 弯曲强度 | MPa | psi | ASTM D790 |
| MPa | psi | ISO 178 | |
| 弯曲模量 | GPa | ksi | ISO 178 |
| GPa | ksi | ASTM D790 | |
| 抗压强度 | MPa | psi | ASTM D695 |
| 泊松比 | ASTM E132 | ||
| 悬壁梁缺口冲击强度 | J/cm @Thickness 3.18 mm | ft-lb/in @Thickness 0.125 in | ASTM D256 |
| 悬壁梁无缺口冲击强度 | J/cm @Thickness 3.18 mm | ft-lb/in @Thickness 0.125 in | ASTM D256 |
| 悬壁梁缺口冲击强度 | kJ/m² | ft-lb/in² | Notch A; ISO 180 |
| 悬壁梁无缺口冲击强度 | kJ/m² | ft-lb/in² | ISO 180 |
| 动态摩擦系数 | vs. Itself; ASTM D1894 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | ohm-cm | ohm-cm | ASTM D257 |
| 表面电阻 | ohm | ohm | ASTM D257 |
| 绝缘电阻 | ohm @Temperature 90.0 °C | ohm @Temperature 194 °F | IEC 60167 |
| 介电常数 | @Frequency 1000 Hz | @Frequency 1000 Hz | ASTM D150 |
| @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | ASTM D150 | |
| 介电强度 | kV/mm | kV/in | ASTM D149 |
| 耗散因数 | @Frequency 1000 Hz | @Frequency 1000 Hz | ASTM D150 |
| @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | ASTM D150 | |
| 相比耐漏电起痕指数(CTI) | V | V | UL 746 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | µm/m-°C @Temperature 100 - 200 °C | µin/in-°F @Temperature 212 - 392 °F | 2 |
| µm/m-°C @Temperature -50.0 - 50.0 °C | µin/in-°F @Temperature -58.0 - 122 °F | 2 | |
| 线性热膨胀系数,横向流动 | µm/m-°C @Temperature -50.0 - 50.0 °C | µin/in-°F @Temperature -58.0 - 122 °F | TMA; ASTM E831 |
| µm/m-°C @Temperature 100 - 200 °C | µin/in-°F @Temperature 212 - 392 °F | TMA; ASTM E831 | |
| 导热系数 | W/m-K | BTU-in/hr-ft²-°F | ASTM C177 |
| 最高工作温度, Air | °C | °F | UL Temperature Rating |
| 载荷下热变形温度(1.8 MPa) | °C | °F | Unannealed; ASTM D648 |
| 可燃性(UL94) | @Thickness 1.60 mm | @Thickness 0.0630 in | |
| 极限氧指数 | ASTM D2863 |
| 材料描述 | 测试方法 | |
|---|---|---|
| 可用性 | Asia Pacific | |
| Europe | ||
| Latin America | ||
| North America | ||
| 颜色 | Natural | |
| 形式 | Pellets | |
| 加工技术 | Injection Molding | |
| 符合RoHS指令 | RoHS Compliant |