Injection Notes: Hot runners: 250°C to 260°C (482°F to 500°F) Drying The material as supplied is ready for molding without drying. However, If the bags have been open for longer than 24 hours, the material needs to be dried. When using a desiccant air dryer with dew point of -28°C (-18°F) or lower, these guidelines can be followed: 0.5-1.5 hour at 120°C (248°F), 1-3 hours at 100°C (212°F), or 1-7 hours at 80°C (176°F). Injection Molding IXEF 1002 compound can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure. The measured melt temperature should be about 280°C (536°F), and the barrel temperatures should be around 250°C to 260°C (482 to 500°F) in the rear zone, gradually increasing to 260 to 290°C (500 to 554°F) in the front zone. If hot runners are used, they should be set to 250 to 260°C (482 to 500°F). To maximize crystallinity, the temperature of the mold cavity surface must be held between 120 and 140°C (248 and 284°F). Molding at lower temperatures will produce articles that may warp, have poor surface appearance, and have a greater tendency to creep. Set injection pressure to give rapid injection. Adjust holding pressure and hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled (95-99%).
Information provided by Solvay Specialty Polymers.| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | ISO 1183 |
| 填料含量 | Glass Fiber Reinforcement | ||
| 吸水率 | @Temperature 23.0 °C, Time 86400 sec | @Temperature 73.4 °F, Time 24.0 hour | ISO 62 |
| 平衡吸湿 | 65% RH; Internal Method | ||
| 线性成型收缩率,Flow | cm/cm | in/in | Internal Method |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | MPa | psi | ISO 527-2 |
| 伸长率 (断裂) | ISO 527-2 | ||
| 拉伸模量 | GPa | ksi | ISO 527-2 |
| 弯曲强度 | MPa | psi | ISO 178 |
| 弯曲模量 | GPa | ksi | ISO 178 |
| 悬壁梁缺口冲击强度 | J/cm | ft-lb/in | ASTM D256 |
| J/cm | ft-lb/in | ASTM D256 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | ohm-cm | ohm-cm | IEC 60093 |
| 介电常数 | @Frequency 110 Hz | @Frequency 110 Hz | IEC 60250 |
| 介电强度 | kV/mm | kV/in | IEC 60243-1 |
| 耗散因数 | @Frequency 110 Hz | @Frequency 110 Hz | IEC 60250 |
| 相比耐漏电起痕指数(CTI) | V | V | IEC 60112 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线性热膨胀系数 | µm/m-°C | µin/in-°F | ISO 11359-2 |
| 载荷下热变形温度(1.8 MPa) | °C | °F | Unannealed; ISO 75-2/A |
| 可燃性(UL94) | UL 94 | ||
| 极限氧指数 | ISO 4589-2 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 料筒后部温度 | °C | °F | |
| 料筒前部温度 | °C | °F | |
| 加工（熔体）温度 | °C | °F | |
| 模具温度 | °C | °F | |
| 干燥温度 | °C | °F | |
| 干燥时间 | hour | hour |
| 材料描述 | 测试方法 | |
|---|---|---|
| 外观 | Black | |
| Colors Available | ||
| Natural Color | ||
| Automotive Specifications | ASTM D6779 PA111G30 | |
| 可用性 | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| 特性 | Good Chemical Resistance | |
| Good Creep Resistance | ||
| Good Dimensional Stability | ||
| High Flow | ||
| High Stiffness | ||
| High Strength | ||
| Low Moisture Absorption | ||
| Outstanding Surface Finish | ||
| 形式 | Pellets | |
| Generic | PARA | |
| 注射速率 | Fast | |
| 加工方法 | Injection Molding | |
| 符合RoHS指令 | RoHS Compliant | |
| 用途 | Appliance Components | |
| Appliances | ||
| Automotive Applications | ||
| Automotive Electronics | ||
| Automotive Exterior Parts | ||
| Automotive Interior Parts | ||
| Automotive Under the Hood | ||
| Bushings | ||
| Camera Applications | ||
| Cell Phones | ||
| Electrical Housing | ||
| Electrical/Electronic Applications | ||
| Furniture | ||
| Gears | ||
| Industrial Applications | ||
| Machine/Mechanical Parts | ||
| Metal Replacement | ||
| Power/Other Tools |