Modified PP for injection moulding with the content of 30% mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased shrinkage. General application in all industry branches - packing material, garden flower-pots, toys, furniture industry, dowels, clamps, hinge, office chairs, hangers, covers of car chassis, fenders, motors etc.
Packaging, transport, stocking
The product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.000 kg palette, in paper octabins with a thick PE foil fixed on a 1.000 kg palette or in other packaging according to customer requirements. The transport is provided in closed-up vehicles where the material is protected against movement and mechanical damage. The product requires stocking in closed-up, dry places protected against sun and thermal radiation.
Information Provided by Plastcom spol. s r.o.| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | |
| 线性成型收缩率 | cm/cm | in/in | |
| 线性成型收缩率，横向 | cm/cm | in/in | |
| 熔体流动速率 | g/10 min @Load 0.325 kg, Temperature 270 °C | g/10 min @Load 0.716 lb, Temperature 518 °F |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | MPa | psi | |
| 伸长率 (断裂) | |||
| 拉伸模量 | GPa | ksi | |
| 弯曲强度 | MPa | psi | |
| 弯曲模量 | GPa | ksi | |
| 简支梁无缺口冲击强度 | J/cm² @Temperature -20.0 °C | ft-lb/in² @Temperature -4.00 °F | |
| @Temperature 23.0 °C | @Temperature 73.4 °F | ||
| 简支梁缺口冲击强度 | J/cm² @Temperature -20.0 °C | ft-lb/in² @Temperature -4.00 °F | |
| J/cm² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度(1.8 MPa) | °C | °F | |
| 维卡软化温度 | °C | °F | B |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | °C | °F | |
| 模具温度 | °C | °F | |
| 干燥温度 | °C | °F | |
| 干燥时间 | hour | hour | |
| 注射压力 | MPa | psi |