Appearance: Red silicone gum and/or rubber on fiberglass cloth
This data represents typical values for the production material. The data should not be used to write, or in place of, material specifications
Information provided by Arlon, Silicone Technologies Division| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | Side 2, Layer 2; Compound Property; Arlon SQA-TMS-024 |
| g/cc | lb/in³ | Side 1 and Side 2, Layer 1; Compound Property; Arlon SQA-TMS-024 | |
| 厚度 | microns | mil | Interleave |
| microns | mil | Side 1; Arlon SQA-TMS-003 | |
| microns | mil | Side 2, Layer 1; Arlon SQA-TMS-003 | |
| microns | mil | Side 2, Layer 2; Arlon SQA-TMS-003 | |
| microns | mil | Substrate; Arlon SQA-TMS-003 | |
| microns | mil | Overall; Arlon SQA-TMS-003 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 A) | Side 2, Layer 2; Compound Property; ASTM D2240 | ||
| Side 1 and Side 2, Layer 1; Compound Property; ASTM D2240 | |||
| 抗张强度 | MPa | psi | Side 1 and Side 2, Layer 1; Compound Property; ASTM D412 |
| MPa | psi | Side 2, Layer 2; Compound Property; ASTM D412 | |
| 伸长率 (断裂) | Side 1 and Side 2, Layer 1; Compound Property; ASTM D412 | ||
| Side 2, Layer 2; Compound Property; ASTM D412 | |||
| 剥离强度 | kN/m | pli | Bond Strength; ASTM D624 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 介电强度 | kV/mm | kV/in | ASTM D149 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 最高工作温度, Air | °C | °F | |
| 最低工作温度, Air | °C | °F | |
| UL RTI | °C | °F | E54153 |
| UL RTI，机械无冲击 | °C | °F | E54153 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 固化时间 | min @Temperature 177 °C | hour @Temperature 350 °F | Recommended Cure Cycle |
| min @Temperature 204 °C | hour @Temperature 400 °F | Recommended Postcure Cycle | |
| 保质期 | Month @Temperature 21.1 °C | Month @Temperature 70.0 °F | From date of manufacture |
| 材料描述 | 测试方法 | |
|---|---|---|
| 颜色 | Red | |
| 产品总重量（oz/yd2） | 36.9 | Arlon SQA-TMS-025 |