Premix Thermoplastics PRE-ELEC® PA 1411 Conductive Thermoplastic Compound

PRE-ELEC® PA 1411 is a conductive thermoplastic compound based on polyamide 6. Conductivity is achieved by using conductive carbon black. PRE-ELEC® PA 1411 has a very low electrical resistivity. PRE-ELEC® 1411 is meant to be used as masterbatch and blended with PA 6.

Applications: Injection moulded housings, boxes and technical parts. PRE-ELEC® PA 1411 is well suited for applications where the good mechanical properties of polyamide are required.

Processing: PRE-ELEC® PA 1411 compound can be processed in the injection moulding machines using normal processing conditions as with polyamide.
Test Specimen: 10[mm] wide moulded rod. Values below also apply to PRE-ELEC® PA 1411 blended with 30% of unreinforced basic PA 6.

Information from Premix OY

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	g/cc	lb/in³
厚度	microns	mil
线性成型收缩率	cm/cm	in/in	ISO 294-4

机械性能	额定值 (公制)	额定值 (英制)	测试方法
肖氏硬度 (邵氏 D)			ISO 868
抗张强度	MPa	psi	ISO 527
抗张强度(屈服)	MPa	psi	ISO 527
伸长率 (断裂)			ISO 527
屈服伸长率			ISO 527
弯曲模量	GPa	ksi	ISO 178
悬壁梁缺口冲击强度	kJ/m² @Thickness 4.00 mm, Temperature -20.0 °C	ft-lb/in² @Thickness 0.157 in, Temperature -4.00 °F	ISO 180
	kJ/m² @Thickness 4.00 mm, Temperature 23.0 °C	ft-lb/in² @Thickness 0.157 in, Temperature 73.4 °F	ISO 180
悬壁梁无缺口冲击强度	@Thickness 4.00 mm, Temperature 23.0 °C	@Thickness 0.157 in, Temperature 73.4 °F	ISO 180
	@Thickness 4.00 mm, Temperature -20.0 °C	@Thickness 0.157 in, Temperature -4.00 °F	ISO 180
简支梁无缺口冲击强度	@Thickness 102 mm, Temperature 23.0 °C	@Thickness 4.00 in, Temperature 73.4 °F	ISO 179
	@Thickness 102 mm, Temperature -20.0 °C	@Thickness 4.00 in, Temperature -4.00 °F	ISO 179
简支梁缺口冲击强度	J/cm² @Thickness 102 mm, Temperature 23.0 °C	ft-lb/in² @Thickness 4.00 in, Temperature 73.4 °F	ISO 179
	J/cm² @Thickness 102 mm, Temperature -20.0 °C	ft-lb/in² @Thickness 4.00 in, Temperature -4.00 °F	ISO 179

电气性能	额定值 (公制)	额定值 (英制)	测试方法
体积电阻率	<= ohm-cm	<= ohm-cm	ISO D-257
表面电阻	<= ohm	<= ohm	ISO IEC 61340-5-1

热性能	额定值 (公制)	额定值 (英制)	测试方法
载荷下热变形温度(0.46 MPa)	°C	°F	75/Method Bf
载荷下热变形温度(1.8 MPa)	°C	°F	75/Method Af
维卡软化温度	°C	°F	ISO 306/B50
	°C	°F	ISO 306/A50

加工性能	额定值 (公制)	额定值 (英制)	测试方法
加工（熔体）温度	°C	°F
模具温度	°C	°F
干燥温度	°C	°F	Pre-drying
干燥时间	hour	hour
注射压力	MPa	psi
保质期	Month	Month	Normal Storing Conditions

材料描述		测试方法
射速	Moderate