Renegade Materials Corporation RM-3002 Bismaleimide (BMI) Resin IM7 12K Carbon Uni-tape

Developed using state-of-the-art formulating technologies, RM-3002 BMI prepreg products deliver superior hot/wet performance in airframe, missile and propulsion applications at service temperatures up to 400°F. RM-3002 “next-generation” BMI delivers improved damage tolerance at higher temperatures vs. industry-standard BMI’s. Renegade precision-quality prepregs exhibit excellent handling characteristics and are available in woven and unidirectional form on various fibers including carbon, quartz and S2 glass. A wide variety of nano-materials can be incorporated into this resin system for tailored laminate properties and multi-functional performance. Renegade offers paste (RM-3006 and RM-3007) and film (RM-3011) adhesives compatible with RM-3002. Renegade also offers similar resin systems for RTM (RM-3000) or VARTM (RM-3010) processing.

Information provided by Renegade Materials Corporation.

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	g/cc	lb/in³	Resin

机械性能	额定值 (公制)	额定值 (英制)	测试方法
伸长率 (断裂)			Resin
弯曲强度	MPa	psi	Resin
弯曲模量	GPa	ksi	Resin
抗压强度	MPa @Temperature 232 °C	psi @Temperature 450 °F	Open Hole, Wet; ASTM D7028
	MPa @Temperature 204 °C	psi @Temperature 400 °F	Open Hole, Wet; ASTM D7028
	MPa @Temperature 177 °C	psi @Temperature 350 °F	Open Hole, Wet; ASTM D7028
	MPa @Temperature 204 °C	psi @Temperature 400 °F	Open Hole, Dry; ASTM D7028
	MPa @Temperature 177 °C	psi @Temperature 350 °F	Open Hole, Dry; ASTM D7028
	MPa @Temperature 21.1 °C	psi @Temperature 70.0 °F	Open Hole, Dry; ASTM D7028
Fracture Toughness	MPa-m½	ksi-in½	Interlaminar, Mode 1, Vf=59.5%; ASTM D5528
	MPa-m½	ksi-in½	Interlaminar, Mode 2, Vf=59.5%; ASTM D5528

热性能	额定值 (公制)	额定值 (英制)	测试方法
玻璃化转变温度，Tg	°C	°F	Storage Modulus, Dry, No post cure, Initial cure at 375°F for 3 hrs
	°C @Temperature 246 °C, Time 21600 sec	°F @Temperature 475 °F, Time 6.00 hour	Storage Modulus, Wet, Vary post cure conditions, cure at 360°F for 6 hrs
	°C @Temperature 191 °C, Time 10800 sec	°F @Temperature 375 °F, Time 3.00 hour	Storage Modulus, Dry, Vary post cure conditions, initial cure at 375°F, 3 hrs
	°C @Temperature 227 °C, Time 21600 sec	°F @Temperature 440 °F, Time 6.00 hour	Storage Modulus, Dry, Vary post cure conditions, initial cure at 375°F, 3 hrs
	°C @Temperature 246 °C, Time 21600 sec	°F @Temperature 475 °F, Time 6.00 hour	Storage Modulus, Dry, Vary post cure conditions, initial cure at 375°F, 3 hrs
	°C @Temperature 227 °C, Time 21600 sec	°F @Temperature 440 °F, Time 6.00 hour	Storage Modulus, Dry, Vary post cure conditions, cure at 360°F for 6 hrs
	°C @Temperature 266 °C, Time 21600 sec	°F @Temperature 510 °F, Time 6.00 hour	Storage Modulus, Dry, Vary post cure conditions, initial cure at 375°F, 3 hrs