Chemically reinforced with 50% glass fiber, suitable for mouldings with high strength and toughness also at low temperatures. Used in the automotive, engineering and electrical industry. With the increasing content of FG also the toughness, tensile and flexural strength increase, the shrinkage decreases and the heat application increases up to 150°C. It achieves higher rates of tensile strength and modulus of elasticity also in conditioning state when compared with PA 6 GF. PA 66 GF 50 achieves modulus - 16000 MPA - of the aluminum alloy rates. Application: hobby tools, covers of electrotools, electromotors, cooling screws of blowers, gear wheels, carrying parts in the automotive industry like brake cables. Delivered in natural and in the full RAL color scale.
Application: Injection Moulding
Information Provided by Plastcom spol. s r.o.| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | STN 64 0111 |
| 线性成型收缩率 | cm/cm | in/in | STN 64 0808 |
| 线性成型收缩率，横向 | cm/cm | in/in | STN 64 0808 |
| 熔体流动速率 | g/10 min @Load 2.16 kg, Temperature 230 °C | g/10 min @Load 4.76 lb, Temperature 446 °F | STN EN ISO 1133 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | MPa | psi | STN EN ISO 527-2 |
| 伸长率 (断裂) | STN EN ISO 527-2 | ||
| 拉伸模量 | GPa | ksi | STN EN ISO 527-2 |
| 弯曲强度 | MPa | psi | STN EN ISO 178 |
| 弯曲模量 | GPa | ksi | STN EN ISO 178 |
| 简支梁无缺口冲击强度 | J/cm² @Temperature -20.0 °C | ft-lb/in² @Temperature -4.00 °F | STN EN ISO 179 |
| J/cm² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | STN EN ISO 179 | |
| 简支梁缺口冲击强度 | J/cm² @Temperature -20.0 °C | ft-lb/in² @Temperature -4.00 °F | STN EN ISO 179 |
| J/cm² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | STN EN ISO 179 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | ohm-cm | ohm-cm | STN IEC 60093 |
| 表面电阻 | ohm | ohm | STN IEC 60093 |
| 介电强度 | kV/mm | kV/in | STN IEC 60243 |
| 相比耐漏电起痕指数(CTI) | V | V | STN 34 6468 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 熔融温度 | °C | °F | DSC; STN EN ISO 3146 |
| 载荷下热变形温度(1.8 MPa) | °C | °F | STN EN ISO 75/A |
| 维卡软化温度 | °C | °F | B; STN EN ISO 306 |
| 可燃性(UL94) | |||
| 灼热丝试验 | °C | °F | STN IEC 60695-2-10 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | °C | °F | |
| 模具温度 | °C | °F | |
| 干燥温度 | °C | °F | |
| 干燥时间 | hour | hour | |
| 水分含量 | STN EN ISO 960 | ||
| 注射压力 | MPa | psi |