| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | DAM; ISO 1183 |
| Water Absorption | @Temperature 23.0 °C | @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to |
| @Temperature 23.0 °C | @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(屈服) | MPa @Temperature 23.0 °C | psi @Temperature 73.4 °F | 50%RH; ISO 527 |
| MPa @Temperature 23.0 °C | psi @Temperature 73.4 °F | DAM; ISO 527 | |
| 伸长率 (断裂) | @Temperature 23.0 °C | @Temperature 73.4 °F | DAM; nominal; ISO 527 |
| @Temperature 23.0 °C | @Temperature 73.4 °F | DAM; ISO 527 | |
| @Temperature 23.0 °C | @Temperature 73.4 °F | 50%RH; nominal; ISO 527 | |
| @Temperature 23.0 °C | @Temperature 73.4 °F | 50%RH; ISO 527 | |
| Elongation at Yield | @Temperature 23.0 °C | @Temperature 73.4 °F | DAM; ISO 527 |
| @Temperature 23.0 °C | @Temperature 73.4 °F | 50%RH; ISO 527 | |
| 拉伸模量 | GPa @Temperature 23.0 °C | ksi @Temperature 73.4 °F | DAM; ISO 527 |
| 简支梁无缺口冲击强度 | @Temperature 23.0 °C | @Temperature 73.4 °F | 50%RH; ISO 179/1eU |
| @Temperature 23.0 °C | @Temperature 73.4 °F | DAM; ISO 179/1eU | |
| 简支梁缺口冲击强度 | J/cm² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA |
| J/cm² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 熔融温度 | °C | °F | 10°C/min; DAM; ISO 11357-1/-3 |
| 载荷下热变形温度(0.46 MPa) | °C | °F | DAM; ISO 75-1/-2 |
| 载荷下热变形温度(1.8 MPa) | °C | °F | DAM; ISO 75-1/-2 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | °C | °F | DAM; Optimum |
| °C | °F | DAM | |
| 干燥温度 | °C | °F | DAM |
| 干燥时间 | hour | hour | DAM |
| 水分含量 | DAM |
| 材料描述 | 测试方法 | |
|---|---|---|
| 形式 | Pellets | DAM |
| Generic | PA66 | DAM |
| Material Status | Preliminary Data | DAM |
| 加工方法 | Injection Molding | DAM |
| 产品分类 | Unreinforced Resins | DAM |
| 符合RoHS指令 | Contact Manufacturer | DAM |