PolyOne Maxxam™ FR PP FR 7B31 Polypropylene, Unspecified (PP, Unspecified)

Polypropylene (PP)

PolyOne Corporation

产品说明

Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V-0, and 5VA performance ratings. In addition, many compounds in the Maxxam FR portfolio offer elevated Relative Thermal Index (RTI) ratings.

Information provided by PolyOne

物理性能额定值 (公制)额定值 (英制)测试方法
比重 g/cc g/cc ASTM D792
熔体流动速率 g/10 min
@Load 2.16 kg, Temperature 230 °C
g/10 min
@Load 4.76 lb, Temperature 446 °F
Procedure A; ASTM D1238
机械性能额定值 (公制)额定值 (英制)测试方法
抗张强度(屈服) MPa psi Type I, 51 mm/min; ASTM D638
伸长率 (断裂) Type I, 51 mm/min; ASTM D638
弯曲模量 GPa ksi ASTM D790
悬壁梁缺口冲击强度 J/cm
@Thickness 3.18 mm, Temperature 23.0 °C
ft-lb/in
@Thickness 0.125 in, Temperature 73.4 °F
Injection Molded; ASTM D256A
热性能额定值 (公制)额定值 (英制)测试方法
载荷下热变形温度(0.46 MPa) °C
@Thickness 3.18 mm
°F
@Thickness 0.125 in
Unannealed; ASTM D648
UL RTI °C
@Thickness 1.50 mm
°F
@Thickness 0.0591 in
UL 746
°C
@Thickness 3.00 mm
°F
@Thickness 0.118 in
UL 746
UL RTI,机械冲击 °C
@Thickness 1.50 mm
°F
@Thickness 0.0591 in
UL 746
°C
@Thickness 3.00 mm
°F
@Thickness 0.118 in
UL 746
UL RTI,机械无冲击 °C
@Thickness 1.50 mm
°F
@Thickness 0.0591 in
UL 746
°C
@Thickness 3.00 mm
°F
@Thickness 0.118 in
UL 746
可燃性(UL94)
@Thickness 0.794 mm
@Thickness 0.0313 in
ALL; UL 94
@Thickness 1.50 mm
@Thickness 0.0591 in
UL 94
@Thickness 3.00 mm
@Thickness 0.118 in
UL 94
材料描述测试方法
添加剂Heat Stabilizer
特性Flame Retardant
Heat Stabilized
High Impact Resistance
Medium Flow
形式Pellets
通用材料PP, Unspecified
通用名Polypropylene, Unspecified (PP, Unspecified)
供货地区 Africa & Middle East
Asia Pacific
Europe
North America
South America
Copyright © souwuxing.com All Rights Reserved. 归 搜聚信息科技公司 所有
此数据表中的信息由 搜聚 从该材料的生产商处获得。搜聚 尽最大努力确保此数据的准确性。 但是 搜聚 对这些数据值不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。
微信小程序 搜物性手机端