| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | g/cc | g/cc | ASTM D792 |
| 线性成型收缩率 | cm/cm @Thickness 3.20 mm | in/in @Thickness 0.126 in | 48 hr, at 80 and 121°C; ASTM D955 |
| cm/cm @Thickness 3.20 mm | in/in @Thickness 0.126 in | 72 hr; ASTM D955 | |
| cm/cm @Thickness 3.20 mm | in/in @Thickness 0.126 in | 48 hr at 121°C; ASTM D955 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | 15 sec delay; ASTM D2240 | ||
| 极限抗拉强度 | MPa | psi | at max load; ASTM D638 |
| 伸长率 (断裂) | ASTM D412 | ||
| 弯曲模量 | GPa | ksi | at 70°C, tangent |
| GPa | ksi | tangent; ASTM D790 | |
| 悬壁梁缺口冲击强度 | J/cm | ft-lb/in | ASTM D256 |
| Falling Dart Impact | J | ft-lb | at -30°C; ASTM D3029 |
| 撕裂强度 | kN/m | pli | ASTM D624 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线性热膨胀系数 | µm/m-°C @Temperature -30.0 - 30.0 °C | µin/in-°F @Temperature -22.0 - 86.0 °F | 2.7 mm/mm; ASTM D696 |
| 熔融温度 | °C | °F | by DSC, 10°C per 220 minutes |
| 载荷下热变形温度(0.46 MPa) | °C @Thickness 3.20 mm | °F @Thickness 0.126 in | ASTM D648 |
| 材料描述 | 测试方法 | |
|---|---|---|
| Heat Sag | 15 mm | ASTM D3769, 1 hr, at 121°C |