Polyfort® FPP 1902 HU is a 10% talc fortified polypropylene. It exhibits high flow and is stabilized for UV resistance.
Information provided by A. Schulman.
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | g/cc | g/cc | ASTM D792 |
| 熔体流动速率 | g/10 min @Temperature 230 °C | g/10 min @Temperature 446 °F | Condition L; ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | ASTM D785 | ||
| 抗张强度(屈服) | MPa | psi | 50 mm/min; ASTM D638 |
| 弯曲模量 | GPa | ksi | ASTM D790 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度(0.46 MPa) | °C | °F | ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | °C | °F | ASTM D648 |