ExxonMobil Bicor™ 52MBR666 OPP Film

Product Description: Bicor 52MBR666 is a biaxially oriented transparent polypropylene film coated with humidity resistant acrylic on both sides. This film is designed to wrap products with a high moisture content or products stored in humid conditions. 52MBR666 is optimized for overwrap applications in paper ream packaging.

Availability: Africa & Middle East, Asia Pacific, Europe, Latin America, North America and South America

Key Features:

• Excellent seal retention on both sides in humid conditions
• Low sealing threshold
• High seal strengths even under low pressure sealing
• Good aroma barrier
• Excellent packaging machine performance
• Outstanding optical properties
• Excellent stiffness
• Ideal support for normal ink systems
• Water-based coatings

Features:

• Broad Seal Range
• Flavor & Aroma Barrier
• Humidity Resistant
• Humidity Resistant Acrylic Coated

Applications:

• Box Overwrap
• Fresh Produce
• Frozen Food
• Health and Beauty Care
• Household and Detergents
• Ice Cream
• Industrial
• Paper Ream wrap

Uses:

• Box Overwrap Flexible Packaging
• HFFS Flexible Packaging
• Pre-made Bags – Flexible Packaging
• VFFS Flexible Packaging

Processing Method: Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print Unsupported

Information provided by ExxonMobil

物理性能	额定值 (公制)	额定值 (英制)	测试方法
Water Vapor Transmission	g/m²/day @Temperature 23.0 °C	g/100 in²/day @Temperature 73.4 °F	85% RH; ExxonMobil Method
	g/m²/day @Temperature 38.0 °C	g/100 in²/day @Temperature 100 °F	90% RH; ExxonMobil Method
Oxygen Transmission Rate	cc/m²/day @Temperature 23.0 °C	cc/100 in²/day @Temperature 73.4 °F	0% RH; ExxonMobil Method
	cc/m²/day @Temperature 23.0 °C	cc/100 in²/day @Temperature 73.4 °F	Wet, 75% RH; ExxonMobil Method
厚度	microns	mil	ExxonMobil Method
Coating Weight	g/m²	lb/ream	ExxonMobil Method

机械性能	额定值 (公制)	额定值 (英制)	测试方法
断裂伸长率，MD			7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
断裂伸长率，TD			7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
弹性模量	GPa	ksi	MD; ExxonMobil Method
	GPa	ksi	TD; ExxonMobil Method
摩擦系数			Both Sides; ExxonMobil Method
Seal Strength	g/25 mm @Pressure 0.00345 MPa, Temperature 100 °C	g/in @Pressure 0.500 psi, Temperature 212 °F	LPS, 0.5 sec; ExxonMobl Method
	g/25 mm @Pressure 0.276 MPa, Temperature 130 °C	g/in @Pressure 40.0 psi, Temperature 266 °F	Otto Bruger, 0.5 sec; ExxonMobl Method
抗张强度(MD : 断裂)	MPa	psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
抗张强度(TD : 断裂)	MPa	psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method

热性能	额定值 (公制)	额定值 (英制)	测试方法
收缩，MD	@Temperature 135 °C, Time 432 sec	@Temperature 275 °F, Time 0.120 hour	ExxonMobil Method
收缩，TD	@Temperature 135 °C, Time 432 sec	@Temperature 275 °F, Time 0.120 hour	ExxonMobil Method

光学性能	额定值 (公制)	额定值 (英制)	测试方法
雾度			ExxonMobil Method
光泽度			45°; ExxonMobil Method

材料描述		测试方法
Heat Seal Range	50°C	36.3 psi (0.25 MPa), 0.2 sec
Yield	14800 in2/lb