Features: Copolymer; Good Flexibility; Low Viscosity
Uses: Wire & Cable Applications
Additional Properties: Crystallization Heat - ASTM D3417 22.0 to 28.0 J/g; Heat of Fusion - ASTM D3417 23.0 to 29.0 J/g
Information provided by Solvay Specialty Polymers.| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | ASTM D792 |
| 吸水率 | @Time 86400 sec | @Time 24.0 hour | ISO 62 |
| 线性成型收缩率,Flow | cm/cm | in/in | |
| 熔体流动速率 | g/10 min @Load 2.16 kg, Temperature 230 °C | g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | ASTM D2240 | ||
| 抗张强度(断裂) | MPa @Thickness 2.00 mm | psi @Thickness 0.0787 in | 50 mm/min; ASTM D638 |
| 抗张强度(屈服) | MPa @Thickness 2.00 mm | psi @Thickness 0.0787 in | 50 mm/min; ASTM D638 |
| 伸长率 (断裂) | 50 mm/min; ASTM D638 | ||
| 屈服伸长率 | 50 mm/min; ASTM D638 | ||
| 拉伸模量 | GPa | ksi | 1.0 mm/min; ASTM D638 |
| 悬壁梁缺口冲击强度 | J/cm @Thickness 4.00 mm | ft-lb/in @Thickness 0.157 in | ASTM D256 |
| 摩擦系数 | vs. Itself; ASTM D1894 | ||
| 动态摩擦系数 | vs. Itself; ASTM D1894 | ||
| 泰伯磨损，毫克/1000次 | CS-10 Wheel, 1000 g; ASTM D1044 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | >= ohm-cm | >= ohm-cm | ASTM D257 |
| 表面电阻 | >= ohm | >= ohm | ASTM D257 |
| 介电常数 | @Frequency 1000 Hz | @Frequency 1000 Hz | ASTM D150 |
| 介电强度 | kV/mm @Thickness 1.00 mm | kV/in @Thickness 0.0394 in | ASTM D149 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | µm/m-°C @Temperature 0.000 - 40.0 °C | µin/in-°F @Temperature 32.0 - 104 °F | 1 |
| 比热容 | J/g-°C @Temperature 23.0 °C | BTU/lb-°F @Temperature 73.4 °F | ASTM C351 |
| J/g-°C @Temperature 100 °C | BTU/lb-°F @Temperature 212 °F | ASTM C351 | |
| 导热系数 | W/m-K @Temperature 23.0 °C | BTU-in/hr-ft²-°F @Temperature 73.4 °F | ASTM C177 |
| 熔融温度 | °C | °F | DSC |
| Crystallization Temperature | °C | °F | Peak; ASTM D3418 |
| 维卡软化温度 | °C | °F | Rate A (50°C/h), Loading 2 (50 N) |
| 玻璃化转变温度，Tg | °C | °F | ASTM E1356 |
| 可燃性(UL94) | @Thickness 0.100 mm | @Thickness 0.00394 in | |
| 极限氧指数 | @Thickness 3.00 mm | @Thickness 0.118 in | ASTM D2863 |
| 材料描述 | 测试方法 | |
|---|---|---|
| 可用性 | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| 形式 | Granules |