Zytel RS 3261THSL BK041A is a renewably sourced polyamide 610 resin containing a minimum of 47% renewably sourced ingredient by weight. It is a black unreinforced toughened and h
Information provided by DuPont Performance Polymers| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | DAM; ISO 1183 |
| 水分吸收 | @Thickness 2.00 mm | @Thickness 0.0787 in | DAM; Sim. to ISO 62 |
| 粘度 | cP @Shear Rate 5000 1/s, Temperature 270 °C | cP @Shear Rate 5000 1/s, Temperature 518 °F | ISO 11403-1 -2 |
| cP @Shear Rate 5000 1/s, Temperature 250 °C | cP @Shear Rate 5000 1/s, Temperature 482 °F | ISO 11403-1 -2 | |
| cP @Shear Rate 5000 1/s, Temperature 240 °C | cP @Shear Rate 5000 1/s, Temperature 464 °F | ISO 11403-1 -2 | |
| cP @Shear Rate 500 1/s, Temperature 270 °C | cP @Shear Rate 500 1/s, Temperature 518 °F | ISO 11403-1 -2 | |
| cP @Shear Rate 500 1/s, Temperature 240 °C | cP @Shear Rate 500 1/s, Temperature 464 °F | ISO 11403-1 -2 | |
| cP @Shear Rate 500 1/s, Temperature 250 °C | cP @Shear Rate 500 1/s, Temperature 482 °F | ISO 11403-1 -2 | |
| 线性成型收缩率,Flow | cm/cm | in/in | DAM; ISO 294-4 2577 |
| 线性成型收缩率，横向 | cm/cm | in/in | DAM; ISO 294-4 2577 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(屈服) | MPa | psi | 50%RH; ISO 527-1/-2 |
| MPa | psi | DAM; ISO 527-1/-2 | |
| 伸长率 (断裂) | DAM; Nominal; ISO 527-1/-2 | ||
| 50%RH; Nominal; ISO 527-1/-2 | |||
| 屈服伸长率 | DAM; ISO 527-1/-2 | ||
| 50%RH; ISO 527-1/-2 | |||
| 拉伸模量 | GPa | ksi | 50%RH; ISO 527-1/-2 |
| GPa | ksi | DAM; ISO 527-1/-2 | |
| 抗剪强度 | MPa @Shear Rate 50.0 1/s, Temperature 270 °C | psi @Shear Rate 50.0 1/s, Temperature 518 °F | ISO 11403-1 -2 |
| MPa @Shear Rate 50.0 1/s, Temperature 250 °C | psi @Shear Rate 50.0 1/s, Temperature 482 °F | ISO 11403-1 -2 | |
| MPa @Shear Rate 50.0 1/s, Temperature 240 °C | psi @Shear Rate 50.0 1/s, Temperature 464 °F | ISO 11403-1 -2 | |
| MPa @Shear Rate 500 1/s, Temperature 270 °C | psi @Shear Rate 500 1/s, Temperature 518 °F | ISO 11403-1 -2 | |
| MPa @Shear Rate 500 1/s, Temperature 240 °C | psi @Shear Rate 500 1/s, Temperature 464 °F | ISO 11403-1 -2 | |
| MPa @Shear Rate 500 1/s, Temperature 250 °C | psi @Shear Rate 500 1/s, Temperature 482 °F | ISO 11403-1 -2 | |
| MPa @Shear Rate 5000 1/s, Temperature 270 °C | psi @Shear Rate 5000 1/s, Temperature 518 °F | ISO 11403-1 -2 | |
| MPa @Shear Rate 5000 1/s, Temperature 250 °C | psi @Shear Rate 5000 1/s, Temperature 482 °F | ISO 11403-1 -2 | |
| MPa @Shear Rate 5000 1/s, Temperature 240 °C | psi @Shear Rate 5000 1/s, Temperature 464 °F | ISO 11403-1 -2 | |
| 悬壁梁缺口冲击强度 | kJ/m² | ft-lb/in² | DAM; Partial; ISO 180/1A |
| kJ/m² | ft-lb/in² | 50%RH; Partial; ISO 180/1A | |
| 简支梁无缺口冲击强度 | DAM; ISO 179/1eU | ||
| 50%RH; ISO 179/1eU | |||
| 简支梁缺口冲击强度 | J/cm² | ft-lb/in² | DAM; Partial; ISO 179/1eA |
| J/cm² | ft-lb/in² | 50%RH; Partial; ISO 179/1eA |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 熔融温度 | °C | °F | DAM; 10°C/min; ISO 11357-1/-3 |
| 载荷下热变形温度(0.46 MPa) | °C | °F | DAM; ISO 75-1/-2 |
| 载荷下热变形温度(1.8 MPa) | °C | °F | DAM; ISO 75-1/-2 |
| 玻璃化转变温度，Tg | °C | °F | DAM; 10°C/min; ISO 11357-1/-2 |
| 材料描述 | 测试方法 | |
|---|---|---|
| Additives | Lubricants | |
| Release agent | ||
| Delivery Form | Pellets | |
| 部件标识代码 | >PA610-I< | ISO 11469 |
| 加工 | Injection Moulding | |
| 供货地区 | Asia Pacific | |
| Europe | ||
| Global | ||
| Near East/Africa | ||
| North America | ||
| South and Central America | ||
| 树脂识别 | PA610-I | ISO 1043 |
| 特殊特性 | Heat stabilised or stable to heat |