Applications: splice enclosures
Description: Higlass BJ22GC conventional melt flow, UV-staibilized, chemically coupled, 30% glass fiber-reinforced polypropylene copolymer was designed for applications which require high impact strength and extended outdoor exposure.
Information provided by Montell Polyolefins.
LyondellBasell is the successor company to Montell.| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | ASTM D792 |
| 熔体流动速率 | g/10 min @Load 2.16 kg, Temperature 230 °C | g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 极限抗拉强度 | MPa | psi | ASTM D638 |
| 伸长率 (断裂) | ASTM D638 | ||
| 弯曲模量 | GPa | ksi | Tangent at 0.05 in/min; ASTM D790A |
| 悬壁梁缺口冲击强度 | J/cm | ft-lb/in | ASTM D256A |
| 悬壁梁无缺口冲击强度 | J/cm | ft-lb/in | ASTM D256A |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度(0.46 MPa) | °C | °F | ASTM D648 |