| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | g/cc | g/cc | ASTM D 792 |
| 吸水率 | @Time 86400 sec | @Time 24.0 hour | ASTM D 570 |
| 线性成型收缩率,Flow | cm/cm @Thickness 3.20 mm | in/in @Thickness 0.126 in | SABIC Method |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | ASTM D 785 | ||
| 抗张强度(屈服) | MPa | psi | Type I, 50 mm/min; ASTM D 638 |
| 弯曲强度 | MPa | psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 弯曲模量 | GPa | ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 悬壁梁缺口冲击强度 | J/cm @Temperature -40.0 °C | ft-lb/in @Temperature -40.0 °F | ASTM D 256 |
| J/cm @Temperature 23.0 °C | ft-lb/in @Temperature 73.4 °F | ASTM D 256 | |
| Gardner Impact | J @Temperature -40.0 °C | ft-lb @Temperature -40.0 °F | ASTM D 3029 |
| J @Temperature -30.0 °C | ft-lb @Temperature -22.0 °F | ASTM D 3029 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 介电常数 | @Frequency 50.0 - 60.0 Hz | @Frequency 50.0 - 60.0 Hz | ASTM D 150 |
| 介电强度 | kV/mm @Thickness 3.20 mm | kV/in @Thickness 0.126 in | in oil; ASTM D 149 |
| 耗散因数 | @Frequency 50.0 - 60.0 Hz | @Frequency 50.0 - 60.0 Hz | ASTM D 150 |
| 耐电弧性 | sec | sec | Tungsten, PLC code 7; ASTM D 495 |
| 相比耐漏电起痕指数(CTI) | V | V | PLC code 3; UL 746A |
| 热丝引燃 (HWI) | sec | sec | PLC code 2; UL 746A |
| 高电弧燃烧，HAI | >= arcs | >= arcs | surface, PLC code 0; UL 746A |
| 高压电弧跟踪率，HVTR | >= mm/min | >= in/min | PLC code 4; UL 746A |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | µm/m-°C @Temperature -40.0 - 95.0 °C | µin/in-°F @Temperature -40.0 - 203 °F | ASTM E 831 |
| 载荷下热变形温度(0.46 MPa) | °C @Thickness 6.40 mm | °F @Thickness 0.252 in | unannealed; ASTM D 648 |
| 载荷下热变形温度(1.8 MPa) | °C @Thickness 6.40 mm | °F @Thickness 0.252 in | unannealed; ASTM D 648 |
| UL RTI | °C | °F | UL 746B |
| UL RTI，机械冲击 | °C | °F | UL 746B |
| UL RTI，机械无冲击 | °C | °F | UL 746B |
| 可燃性(UL94) | @Thickness 1.47 mm | @Thickness 0.0579 in | UL 94 |