Forms: Pellets
Additive: PTFE Lubricant
Features: Lubricated
Information provided by TP Composites, Inc.| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | ASTM D792 |
| 线性成型收缩率,Flow | cm/cm @Thickness 3.17 mm | in/in @Thickness 0.125 in | ASTM D955 |
| 熔体流动速率 | g/10 min @Load 3.80 kg, Temperature 230 °C | g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | ASTM D785 | ||
| 抗张强度(屈服) | MPa | psi | ASTM D638 |
| 伸长率 (断裂) | ASTM D638 | ||
| 弯曲强度 | MPa | psi | ASTM D790 |
| 弯曲模量 | GPa | ksi | ASTM D790 |
| 悬壁梁缺口冲击强度 | J/cm @Thickness 3.17 mm, Temperature -40.0 °C | ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F | ASTM D256 |
| J/cm @Thickness 3.17 mm, Temperature 0.000 °C | ft-lb/in @Thickness 0.125 in, Temperature 32.0 °F | ASTM D256 | |
| J/cm @Thickness 3.17 mm, Temperature 22.8 °C | ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F | ASTM D256 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度(0.46 MPa) | °C | °F | Unannealed; ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | °C | °F | Unannealed; ASTM D648 |