ExxonMobil Santoprene® 201-87 Thermoplastic Elastomer

A hard, colorable, versatile thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in a wide range of applications. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding, extrusion or blow molding. It is polyolefin based and completely recyclable.

Key Features:

• UL listed: file #QMFZ2.E80017, Plastics - Component; file #QMFZ8.E80017, Plastics Certified For Canada - Component.
• Although not NSF certified, this product has a Material Supplier Form on file with NSF to facilitate its evaluation for use in applications requiring NSF certification.
• Recommended for applications requiring excellent flex fatigue resistance.
• Excellent ozone resistance.
• EU and China RoHS compliant.

Applications:

• Automotive-Boots and Bellows for Steering and Suspension

Uses:

• Appliance Components
• Automotive Applications
• Automotive Under the Hood
• Consumer Applications
• Diaphrams
• Electrical Parts
• Living Hinges
• Tubing

Availability: Africa & Middle East, Europe, North America, Asia Pacific, Latin America and South America

Information provided by Advanced Elastomer Systems

物理性能	额定值 (公制)	额定值 (英制)	测试方法
比重	g/cc	g/cc	23°C; ASTM D792
处理

机械性能	额定值 (公制)	额定值 (英制)	测试方法
肖氏硬度 (邵氏 A)			2 mm, 15 sec; ISO 868
			in Air 150°C, 168 hr; ASTM D573
抗张强度(断裂)	MPa	psi	in Air 150°C, 168 hr; ASTM D573
	MPa	psi	Across Flow; ASTM D412
抗张强度	MPa @Strain 100 %	psi @Strain 100 %	Across Flow; ASTM D412
伸长率 (断裂)			in Air 150°C, 168 hr; ASTM D573
			Across Flow; ASTM D412
撕裂强度	kN/m	pli	73°F, Die C; ASTM D624
永久压缩			158°F, 22 hr; ASTM D395
			257°F, 70 hr; ASTM D395

电气性能	额定值 (公制)	额定值 (英制)	测试方法
介电常数	@Thickness 2.03 mm	@Thickness 0.0799 in	ASTM D150
介电强度	kV/mm @Thickness 2.03 mm	kV/in @Thickness 0.0799 in	ASTM D149

热性能	额定值 (公制)	额定值 (英制)	测试方法
脆化温度	°C	°F	ASTM D746
UL RTI	°C	°F	UL 746
UL RTI，机械冲击	°C @Thickness 1.00 mm	°F @Thickness 0.0394 in	UL 746
	°C @Thickness 1.50 mm	°F @Thickness 0.0591 in	UL 746
	°C @Thickness 3.00 mm	°F @Thickness 0.118 in	UL 746
可燃性(UL94)	@Thickness 1.00 mm	@Thickness 0.0394 in
	@Thickness 1.50 mm	@Thickness 0.0591 in
	@Thickness 3.00 mm	@Thickness 0.118 in

加工性能	额定值 (公制)	额定值 (英制)	测试方法
加工温度	°C	°F
料筒后部温度	°C	°F
料筒中部温度	°C	°F
料筒前部温度	°C	°F
射嘴温度	°C	°F
模具温度	°C	°F
加工（熔体）温度	°C	°F	Extrusion
	°C	°F	Processing
模具温度	°C	°F
干燥温度	°C	°F
干燥时间	hour	hour
背压	MPa	psi	Injection
	MPa	psi	Extrusion
Clamp Pressure	MPa	psi
Vent Depth	cm	in
填料	cm	in
螺杆转速	rpm	rpm

材料描述		测试方法
颜色	Natural Color
形式	Pellets
注射速率	Fast
Screw Compression Ratio	2:1 - 2.5:1
Screw L/D Ratio	16:1 - 20:1
Suggested Max Regrind	20%