| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | g/cc | g/cc | DAM; ASTM D792 |
| 密度 | g/cc | lb/in³ | DAM; ISO 1183 |
| 填料含量 | DAM | ||
| Water Absorption | @Thickness 1.00 mm, Temperature 23.0 °C | @Thickness 0.0394 in, Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to |
| @Thickness 1.00 mm, Temperature 23.0 °C | @Thickness 0.0394 in, Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |
| 线性成型收缩率 | cm/cm @Thickness 3.20 mm | in/in @Thickness 0.126 in | Flow; DAM |
| cm/cm @Thickness 3.20 mm | in/in @Thickness 0.126 in | Transverse; DAM |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | MPa @Temperature 23.0 °C | psi @Temperature 73.4 °F | DAM; ISO 527 |
| 抗张强度 | MPa @Temperature 23.0 °C | psi @Temperature 73.4 °F | 50%RH; ASTM D638 |
| MPa @Temperature 23.0 °C | psi @Temperature 73.4 °F | DAM; ASTM D638 | |
| 伸长率 (断裂) | @Temperature 23.0 °C | @Temperature 73.4 °F | DAM; ASTM D638 |
| @Temperature 23.0 °C | @Temperature 73.4 °F | DAM; ISO 527 | |
| @Temperature 23.0 °C | @Temperature 73.4 °F | 50%RH; ASTM D638 | |
| 拉伸模量 | GPa @Temperature 23.0 °C | ksi @Temperature 73.4 °F | DAM; ISO 527 |
| 弯曲强度 | MPa @Temperature 23.0 °C | psi @Temperature 73.4 °F | 50%RH; ASTM D790 |
| MPa @Temperature 23.0 °C | psi @Temperature 73.4 °F | DAM; ASTM D790 | |
| 弯曲模量 | GPa @Temperature 23.0 °C | ksi @Temperature 73.4 °F | 50%RH; ASTM D790 |
| GPa @Temperature 23.0 °C | ksi @Temperature 73.4 °F | DAM; ISO 178 | |
| GPa @Temperature 23.0 °C | ksi @Temperature 73.4 °F | DAM; ASTM D790 | |
| 悬壁梁缺口冲击强度 | J/cm @Temperature 23.0 °C | ft-lb/in @Temperature 73.4 °F | 50%RH; ASTM D256 |
| J/cm @Temperature 23.0 °C | ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | |
| Izod Impact, Unnotched | J/cm @Temperature 23.0 °C | ft-lb/in @Temperature 73.4 °F | DAM; ASTM D4812 |
| J/cm @Temperature 23.0 °C | ft-lb/in @Temperature 73.4 °F | 50%RH; ASTM D4812 | |
| 悬壁梁缺口冲击强度 | kJ/m² @Temperature -40.0 °C | ft-lb/in² @Temperature -40.0 °F | DAM; ISO 180/1A |
| kJ/m² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |
| 简支梁缺口冲击强度 | J/cm² @Temperature -40.0 °C | ft-lb/in² @Temperature -40.0 °F | DAM; ISO 179/1eA |
| J/cm² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | |
| J/cm² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 相比耐漏电起痕指数(CTI) | V @Temperature 23.0 °C | V @Temperature 73.4 °F | DAM; IEC 60112 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | µm/m-°C @Temperature 23.0 - 55.0 °C | µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 |
| 线性热膨胀系数,横向流动 | µm/m-°C @Temperature 23.0 - 55.0 °C | µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 |
| 熔融温度 | °C | °F | 10°C/min; DAM; ISO 11357-1/-3 |
| °C | °F | DAM; ASTM D3418 | |
| 载荷下热变形温度(0.46 MPa) | °C | °F | DAM; ASTM D648 |
| °C | °F | DAM; ISO 75-1/-2 | |
| 载荷下热变形温度(1.8 MPa) | °C | °F | DAM; ISO 75-1/-2 |
| °C | °F | DAM; ASTM D648 | |
| UL RTI | °C @Thickness 3.00 mm | °F @Thickness 0.118 in | DAM; UL 746B |
| °C @Thickness 0.750 mm | °F @Thickness 0.0295 in | DAM; UL 746B | |
| °C @Thickness 1.50 mm | °F @Thickness 0.0591 in | DAM; UL 746B | |
| UL RTI，机械冲击 | °C @Thickness 0.750 mm | °F @Thickness 0.0295 in | DAM; UL 746B |
| °C @Thickness 1.50 mm | °F @Thickness 0.0591 in | DAM; UL 746B | |
| °C @Thickness 3.00 mm | °F @Thickness 0.118 in | DAM; UL 746B | |
| UL RTI，机械无冲击 | °C @Thickness 0.750 mm | °F @Thickness 0.0295 in | DAM; UL 746B |
| °C @Thickness 1.50 mm | °F @Thickness 0.0591 in | DAM; UL 746B | |
| °C @Thickness 3.00 mm | °F @Thickness 0.118 in | DAM; UL 746B | |
| 可燃性(UL94) | @Thickness 1.50 mm | @Thickness 0.0591 in | DAM; IEC 60695-11-10 |
| @Thickness 3.00 mm | @Thickness 0.118 in | DAM; IEC 60695-11-10 | |
| @Thickness 0.750 mm | @Thickness 0.0295 in | DAM; IEC 60695-11-10 | |
| @Thickness 1.50 mm | @Thickness 0.0591 in | DAM; UL94 | |
| @Thickness 3.00 mm | @Thickness 0.118 in | DAM; UL94 | |
| @Thickness 0.750 mm | @Thickness 0.0295 in | DAM; UL94 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | °C | °F | DAM; Optimum |
| °C | °F | DAM | |
| 模具温度 | °C | °F | DAM |
| °C | °F | DAM; optimum | |
| 干燥温度 | °C | °F | DAM |
| 干燥时间 | hour | hour | DAM |
| 水分含量 | DAM |
| 材料描述 | 测试方法 | |
|---|---|---|
| 外观 | Black Color | DAM |
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| 特性 | Heat Stabilized | DAM |
| Heat Stabilized | DAM | |
| Filler | Glass fiber reinforcement | DAM |
| 形式 | Pellets | DAM |
| Generic | Nylon 612 | DAM |
| Material Status | Current | DAM |
| 部件标识代码 | >PA612-GF33< | ISO 11469; DAM |
| Polymer Family | Polyamide | DAM |
| Polymer Type | PA612 | DAM |
| 加工方法 | Injection Molding | DAM |
| 产品分类 | Color Stable Resins | DAM |
| Encapsulation Resins | DAM | |
| Glass Reinforced Resins | DAM | |
| Region Available - Global | Yes | DAM |
| 树脂识别 | PA612-GF33 | ISO 1043; DAM |
| 符合RoHS指令 | Contact Manufacturer | DAM |
| 用途 | Electrical/Electronic Applications | DAM |
| Electrical/Electronic Applications | DAM |