| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 A) | Original Properties; ASTM D2240 | ||
| @Temperature 23.0 °C | @Temperature 73.4 °F | ASTM Reference Fuel B Immersion, 70 hours; ASTM D2240 | |
| @Temperature 23.0 °C | @Temperature 73.4 °F | ASTM Fuel A Immersion, 70 hours; ASTM D2240 | |
| @Temperature 100 °C | @Temperature 212 °F | Air Aging, 70 hours; ASTM D2240 | |
| @Temperature 100 °C | @Temperature 212 °F | ASTM IRM-903 Oil Immersion, 70 hours; ASTM D2240 | |
| @Temperature 100 °C | @Temperature 212 °F | Water Resistance, 70 hours; ASTM D2240 | |
| 极限抗拉强度 | MPa | psi | Original Properties; ASTM D412 Die C |
| MPa @Temperature 23.0 °C | psi @Temperature 73.4 °F | ASTM Reference Fuel B Immersion, 70 hours; ASTM D412 Die C | |
| MPa @Temperature 23.0 °C | psi @Temperature 73.4 °F | ASTM Fuel A Immersion, 70 hours; ASTM D412 Die C | |
| MPa @Temperature 100 °C | psi @Temperature 212 °F | Air Aging, 70 hours; ASTM D412 Die C | |
| MPa @Temperature 100 °C | psi @Temperature 212 °F | ASTM IRM-903 Oil Immersion, 70 hours; ASTM D412 Die C | |
| 伸长率 (断裂) | Original Properties; ASTM D412 Die C | ||
| @Temperature 23.0 °C | @Temperature 73.4 °F | ASTM Reference Fuel B Immersion, 70 hours; ASTM D412 Die C | |
| @Temperature 100 °C | @Temperature 212 °F | Air Aging, 70 hours; ASTM D412 Die C | |
| @Temperature 100 °C | @Temperature 212 °F | ASTM IRM-903 Oil Immersion, 70 hours; ASTM D412 Die C | |
| @Temperature 23.0 °C | @Temperature 73.4 °F | ASTM Fuel A Immersion, 70 hours; ASTM D412 Die C | |
| 永久压缩 | @Temperature 100 °C, Time 79200 sec | @Temperature 212 °F, Time 22.0 hour | ASTM D395 |
| 材料描述 | 测试方法 | |
|---|---|---|
| Volume Change (%), ASTM D471 | -1.1 | ASTM IRM-903 Oil Immersion, 70 hours at 100°C |
| -1.2 | ASTM Fuel A Immersion, 70 hours at 23°C | |
| 17.1 | ASTM Reference Fuel B Immersion, 70 hours at 23°C | |
| -4.8 | Water Resistance, 70 hours at 100°C |