LNP ULTEM® UCF1205 Polyetherimide, 12% Carbon Fiber Reinforcement, 5% PTFE Lubricant

Polyetherimide (PEI), Carbon Fiber Filled

产品说明

Office equipment internal parts.

Information provided by LNP, a GE Plastics Company.

This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.

物理性能额定值 (公制)额定值 (英制)测试方法
比重 g/cc g/cc ASTM D792
机械性能额定值 (公制)额定值 (英制)测试方法
抗张强度(断裂) MPa psi Type I, 5 mm/min; ASTM D638
抗张强度(屈服) MPa psi Type I, 5 mm/min; ASTM D638
伸长率 (断裂) Type I, 5 mm/min; ASTM D638
拉伸模量 GPa ksi 5 mm/min; ASTM D638
弯曲强度 MPa psi 50.8 mm Span, 1 mm/min; ASTM D790
弯曲模量 GPa ksi (50.8 mm Span) 1mm/min; ASTM D790
悬壁梁缺口冲击强度 J/cm ft-lb/in ASTM D256
悬壁梁无缺口冲击强度 J/cm ft-lb/in ASTM D256
Falling Dart Impact J ft-lb ASTM D3763
电气性能额定值 (公制)额定值 (英制)测试方法
体积电阻率 ohm-cm ohm-cm ASTM D257
表面电阻 ASTM D257
热性能额定值 (公制)额定值 (英制)测试方法
载荷下热变形温度(0.46 MPa) °C
@Thickness 3.18 mm
°F
@Thickness 0.125 in
Unannealed; ASTM D648
载荷下热变形温度(1.8 MPa) °C
@Thickness 3.18 mm
°F
@Thickness 0.125 in
Unannealed; ASTM D648
加工性能额定值 (公制)额定值 (英制)测试方法
料筒后部温度 °C °F
料筒中部温度 °C °F
料筒前部温度 °C °F
射嘴温度 °C °F
加工(熔体)温度 °C °F
模具温度 °C °F
干燥温度 °C °F
干燥时间<= hour <= hour
水分含量 Suggested
背压 MPa psi
Clamp Pressure MPa psi
Shot Size Suggested
Vent Depth cm in
螺杆转速 rpm rpm
Copyright © souwuxing.com All Rights Reserved. 归 搜聚信息科技公司 所有
此数据表中的信息由 搜聚 从该材料的生产商处获得。搜聚 尽最大努力确保此数据的准确性。 但是 搜聚 对这些数据值不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。