Available in Americas, Europe, Middle East, Africa, India and Asia
Data provided by Lubrizol
Lubrizol acquired the Isoplast product line from Dow in 2009.| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | ASTM D792 |
| 吸水率 | 24 hrs at 23°C; ASTM D570 | ||
| 线性成型收缩率 | cm/cm | in/in | ASTM D955 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | ASTM D648 | ||
| 极限抗拉强度 | MPa | psi | ASTM D638 |
| 抗张强度(屈服) | MPa | psi | ASTM D638 |
| 伸长率 (断裂) | ASTM D638 | ||
| 屈服伸长率 | ASTM D638 | ||
| 拉伸模量 | GPa | ksi | ASTM D638 |
| 弯曲强度 | MPa | psi | ASTM D790 |
| 弯曲模量 | GPa | ksi | ASTM D790 |
| Izod Impact, Unnotched | J/cm @Thickness 3.20 mm, Temperature -40.0 °C | ft-lb/in @Thickness 0.126 in, Temperature -40.0 °F | ASTM D256 |
| J/cm @Thickness 6.40 mm, Temperature 23.0 °C | ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F | ASTM D256 | |
| J/cm @Thickness 3.20 mm, Temperature 23.0 °C | ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 | |
| Dart Drop, Total Energy | J @Temperature 23.0 °C | ft-lb @Temperature 73.4 °F | ASTM D3763 |
| J @Temperature -29.0 °C | ft-lb @Temperature -20.2 °F | ASTM D3763 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线性热膨胀系数 | µm/m-°C @Temperature 20.0 °C | µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| 载荷下热变形温度(0.46 MPa) | °C | °F | Unannealed; ASTM D648 |
| °C | °F | Annealed; ASTM D648 | |
| 载荷下热变形温度(1.8 MPa) | °C | °F | Unannealed; ASTM D648 |
| °C | °F | Annealed; ASTM D648 | |
| 维卡软化温度 | °C | °F | ASTM D1525 |
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 光泽度 | Gardner Gloss, 60°; ASTM D823 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | °C | °F | |
| 模具温度 | °C | °F | |
| 干燥温度 | °C | °F |