Zytel 70G30HSL NC010 is a 30% glass fiber reinforced heat stabilized polyamide 66 resin for injection molding.
Information provided by DuPont Performance Polymers| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | DAM; ISO 1183 |
| 吸水率 | @Thickness 2.00 mm | @Thickness 0.0787 in | DAM; Sim. to ISO 62 |
| 水分吸收 | @Thickness 2.00 mm | @Thickness 0.0787 in | DAM; Sim. to ISO 62 |
| 粘度 | cP @Shear Rate 5000 1/s, Temperature 305 °C | cP @Shear Rate 5000 1/s, Temperature 581 °F | ISO 11403-1 -2 |
| cP @Shear Rate 5000 1/s, Temperature 295 °C | cP @Shear Rate 5000 1/s, Temperature 563 °F | ISO 11403-1 -2 | |
| cP @Shear Rate 5000 1/s, Temperature 285 °C | cP @Shear Rate 5000 1/s, Temperature 545 °F | ISO 11403-1 -2 | |
| cP @Shear Rate 500 1/s, Temperature 305 °C | cP @Shear Rate 500 1/s, Temperature 581 °F | ISO 11403-1 -2 | |
| cP @Shear Rate 500 1/s, Temperature 295 °C | cP @Shear Rate 500 1/s, Temperature 563 °F | ISO 11403-1 -2 | |
| cP @Shear Rate 500 1/s, Temperature 285 °C | cP @Shear Rate 500 1/s, Temperature 545 °F | ISO 11403-1 -2 | |
| 线性成型收缩率,Flow | cm/cm | in/in | DAM; ISO 294-4 2577 |
| 线性成型收缩率，横向 | cm/cm | in/in | DAM; ISO 294-4 2577 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（M 级） | 50%RH; ISO 2039-2 | ||
| DAM; ISO 2039-2 | |||
| 洛氏硬度（R 级） | 50%RH; ISO 2039-2 | ||
| DAM; ISO 2039-2 | |||
| 抗张强度(断裂) | MPa | psi | 50%RH; ISO 527-1/-2 |
| MPa | psi | DAM; ISO 527-1/-2 | |
| 伸长率 (断裂) | DAM; ISO 527-1/-2 | ||
| 50%RH; ISO 527-1/-2 | |||
| 拉伸模量 | GPa | ksi | 50%RH; ISO 527-1/-2 |
| GPa | ksi | DAM; ISO 527-1/-2 | |
| 剪切模量 | GPa @Temperature 150 °C | ksi @Temperature 302 °F | DAM; Dynamic; ISO 11403-1 -2 |
| GPa @Temperature 110 °C | ksi @Temperature 230 °F | DAM; Dynamic; ISO 11403-1 -2 | |
| GPa @Temperature 60.0 °C | ksi @Temperature 140 °F | DAM; Dynamic; ISO 11403-1 -2 | |
| GPa @Temperature 10.0 °C | ksi @Temperature 50.0 °F | DAM; Dynamic; ISO 11403-1 -2 | |
| GPa @Temperature -20.0 °C | ksi @Temperature -4.00 °F | DAM; Dynamic; ISO 11403-1 -2 | |
| GPa @Temperature -50.0 °C | ksi @Temperature -58.0 °F | DAM; Dynamic; ISO 11403-1 -2 | |
| 悬壁梁缺口冲击强度 | kJ/m² | ft-lb/in² | DAM; ISO 180/1A |
| kJ/m² | ft-lb/in² | 50%RH; ISO 180/1A | |
| kJ/m² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 180/1A | |
| kJ/m² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | DAM; ISO 180/1A | |
| 简支梁无缺口冲击强度 | J/cm² | ft-lb/in² | DAM; ISO 179/1eU |
| J/cm² | ft-lb/in² | 50%RH; ISO 179/1eU | |
| J/cm² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eU | |
| J/cm² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eU | |
| 简支梁缺口冲击强度 | J/cm² | ft-lb/in² | DAM; ISO 179/1eA |
| J/cm² | ft-lb/in² | 50%RH; ISO 179/1eA | |
| J/cm² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | |
| J/cm² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eA | |
| 拉伸蠕变模量(1 hr) | MPa @Time 3600 sec | psi @Time 1.00 hour | 50%RH; ISO 899-1 |
| 拉伸蠕变模量(1000 hr) | MPa @Time 3.60e+6 sec | psi @Time 1000 hour | 50%RH; ISO 899-1 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | ohm-cm | ohm-cm | 50%RH; IEC 60093 |
| >= ohm-cm | >= ohm-cm | DAM; IEC 60093 | |
| 表面电阻 | ohm | ohm | 50%RH; IEC 60093 |
| ohm | ohm | DAM; ASTM D257 | |
| 介电常数 | @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | DAM; IEC 60250 |
| @Frequency 100 Hz | @Frequency 100 Hz | DAM; IEC 60250 | |
| @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | 50%RH; IEC 60250 | |
| @Frequency 100 Hz | @Frequency 100 Hz | 50%RH; IEC 60250 | |
| 介电强度 | kV/mm | kV/in | 50%RH; IEC 60243-1 |
| kV/mm | kV/in | DAM; IEC 60243-1 | |
| 耗散因数 | @Frequency 100 Hz | @Frequency 100 Hz | DAM; IEC 60250 |
| @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | DAM; IEC 60250 | |
| @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | 50%RH; IEC 60250 | |
| @Frequency 100 Hz | @Frequency 100 Hz | 50%RH; IEC 60250 | |
| 相比耐漏电起痕指数(CTI) | V | V | DAM; IEC 60112 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | µm/m-°C | µin/in-°F | DAM; ISO 11359-1/-2 |
| 线性热膨胀系数,横向流动 | µm/m-°C | µin/in-°F | DAM; ISO 11359-1/-2 |
| 熔融温度 | °C | °F | DAM; 10°C/min; ISO 11357-1/-3 |
| 载荷下热变形温度(0.46 MPa) | °C | °F | DAM; ISO 75-1/-2 |
| 载荷下热变形温度(1.8 MPa) | °C | °F | DAM; ISO 75-1/-2 |
| 可燃性(UL94) | @Thickness 1.50 mm | @Thickness 0.0591 in | DAM; IEC 60695-11-10 |
| @Thickness 0.800 mm | @Thickness 0.0315 in | DAM; IEC 60695-11-10 | |
| Flame Spread | mm/min @Thickness 1.00 mm | in/min @Thickness 0.0394 in | ISO 3795 (FMVSS 302) |
| 材料描述 | 测试方法 | |
|---|---|---|
| 部件标识代码 | >PA66-GF30< | ISO 11469 |
| 加工 | Injection Moulding | |
| 供货地区 | Europe | |
| Near East/Africa | ||
| 树脂识别 | PA66-GF30 | |
| 特殊特性 | Heat stabilised or stable to heat | |
| UL recognition | UL | DAM |