| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | g/cc @Temperature 218 °C | lb/in³ @Temperature 425 °F | |
| g/cc @Temperature 177 °C | lb/in³ @Temperature 350 °F | ||
| g/cc @Temperature 121 °C | lb/in³ @Temperature 250 °F | ||
| g/cc @Temperature 65.6 °C | lb/in³ @Temperature 150 °F | ||
| g/cc @Temperature 23.9 °C | lb/in³ @Temperature 75.0 °F | ||
| g/cc @Temperature 15.6 °C | lb/in³ @Temperature 60.0 °F | ||
| g/cc @Temperature -17.8 °C | lb/in³ @Temperature 0.000 °F | ||
| g/cc @Temperature -45.6 °C | lb/in³ @Temperature -50.0 °F | ||
| g/cc @Temperature -73.3 °C | lb/in³ @Temperature -100 °F | ||
| 粘度 | cP @Temperature 218 °C | cP @Temperature 425 °F | |
| cP @Temperature 177 °C | cP @Temperature 350 °F | ||
| cP @Temperature 121 °C | cP @Temperature 250 °F | ||
| cP @Temperature 65.6 °C | cP @Temperature 150 °F | ||
| cP @Temperature -17.8 °C | cP @Temperature 0.000 °F | ||
| cP @Temperature 23.9 °C | cP @Temperature 75.0 °F | ||
| cP @Temperature -45.6 °C | cP @Temperature -50.0 °F | ||
| cP @Temperature -73.3 °C | cP @Temperature -100 °F | ||
| Viscosity Measure | cSt @Temperature 218 °C | cSt @Temperature 425 °F | |
| cSt @Temperature 177 °C | cSt @Temperature 350 °F | ||
| cSt @Temperature 121 °C | cSt @Temperature 250 °F | ||
| cSt @Temperature 65.6 °C | cSt @Temperature 150 °F | ||
| cSt @Temperature 23.9 °C | cSt @Temperature 75.0 °F | ||
| cSt @Temperature -17.8 °C | cSt @Temperature 0.000 °F | ||
| cSt @Temperature -45.6 °C | cSt @Temperature -50.0 °F | ||
| cSt @Temperature -73.3 °C | cSt @Temperature -100 °F | ||
| 分子量 | g/mol | g/mol | average |
| 蒸汽压力 | bar @Temperature 65.6 °C | torr @Temperature 150 °F | |
| bar @Temperature 121 °C | torr @Temperature 250 °F | ||
| bar @Temperature 177 °C | torr @Temperature 350 °F | ||
| bar @Temperature 218 °C | torr @Temperature 425 °F |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | ohm-cm | ohm-cm | |
| 介电常数 | @Frequency 1000 Hz | @Frequency 1000 Hz | ASTM D924-04 |
| 介电击穿 | V @Thickness 2.54 mm | V @Thickness 0.100 in | ASTM D1816-04 |
| 耗散因数 | @Frequency 1000 Hz | @Frequency 1000 Hz | ASTM D924-04 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| Heat of Vaporization | J/g | BTU/lb | |
| 比热容 | J/g-°C @Temperature -73.3 °C | BTU/lb-°F @Temperature -100 °F | |
| J/g-°C @Temperature -45.6 °C | BTU/lb-°F @Temperature -50.0 °F | ||
| J/g-°C @Temperature -17.8 °C | BTU/lb-°F @Temperature 0.000 °F | ||
| J/g-°C @Temperature 23.9 °C | BTU/lb-°F @Temperature 75.0 °F | ||
| J/g-°C @Temperature 65.6 °C | BTU/lb-°F @Temperature 150 °F | ||
| J/g-°C @Temperature 121 °C | BTU/lb-°F @Temperature 250 °F | ||
| J/g-°C @Temperature 177 °C | BTU/lb-°F @Temperature 350 °F | ||
| J/g-°C @Temperature 218 °C | BTU/lb-°F @Temperature 425 °F | ||
| 导热系数 | W/m-K @Temperature 218 °C | BTU-in/hr-ft²-°F @Temperature 425 °F | |
| W/m-K @Temperature 177 °C | BTU-in/hr-ft²-°F @Temperature 350 °F | ||
| W/m-K @Temperature 121 °C | BTU-in/hr-ft²-°F @Temperature 250 °F | ||
| W/m-K @Temperature 65.6 °C | BTU-in/hr-ft²-°F @Temperature 150 °F | ||
| W/m-K @Temperature 23.9 °C | BTU-in/hr-ft²-°F @Temperature 75.0 °F | ||
| W/m-K @Temperature -17.8 °C | BTU-in/hr-ft²-°F @Temperature 0.000 °F | ||
| W/m-K @Temperature -45.6 °C | BTU-in/hr-ft²-°F @Temperature -50.0 °F | ||
| W/m-K @Temperature -73.3 °C | BTU-in/hr-ft²-°F @Temperature -100 °F | ||
| 沸点 | °C | °F | |
| 最高工作温度, Air | °C | °F | |
| °C | °F | max. recommended film temperature | |
| 最低工作温度, Air | °C | °F | |
| Flash Point | >= °C | >= °F | closed cup; ASTM D56 |
| 材料描述 | 测试方法 | |
|---|---|---|
| 外观 | water white | |
| Autoignition | >430°F | < 10 sec delay |
| Chemistry | synthetic hydrocarbon blend | |
| Odor | sweet |