Cadi 2 MOLD-MOR™

A very hard heat treatable beryllium-copper alloy with moderate electrical conductivity. C17510 can be utilized when a combination of very good mechanical strength along with moderate electrical and thermal electrical conductivity are required.

Forms:

• Rod
• Bar
• Plate

Information provided by Cadi Company.

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	g/cc	lb/in³

机械性能	额定值 (公制)	额定值 (英制)	测试方法
洛氏硬度（B 级）			Any thickness
抗张强度(断裂)	>= MPa @Thickness >=50.8 mm	>= psi @Thickness >=2.00 in
	>= MPa @Thickness 25.4 - 50.8 mm	>= psi @Thickness 1.00 - 2.00 in
	>= MPa @Thickness <=25.4 mm	>= psi @Thickness <=1.00 in
抗张强度(屈服)	>= MPa @Strain 0.500 %, Thickness >=50.8 mm	>= psi @Strain 0.500 %, Thickness >=2.00 in
	>= MPa @Strain 0.500 %, Thickness 25.4 - 50.8 mm	>= psi @Strain 0.500 %, Thickness 1.00 - 2.00 in
	>= MPa @Strain 0.500 %, Thickness <=25.4 mm	>= psi @Strain 0.500 %, Thickness <=1.00 in
弹性模量	GPa	ksi
泊松比
剪切模量	GPa	ksi

电气性能	额定值 (公制)	额定值 (英制)	测试方法
电阻率	<= ohm-cm	<= ohm-cm	Calculated from Min 45 %IACS, up to 3" diameter/any thickness

热性能	额定值 (公制)	额定值 (英制)	测试方法
导热系数	W/m-K	BTU-in/hr-ft²-°F
熔融温度	°C	°F
固相线	°C	°F
液相线	°C	°F

加工性能	额定值 (公制)	额定值 (英制)	测试方法
加工温度	°C	°F	Brazing

构成要素属性	额定值 (公制)	额定值 (英制)	测试方法
Beryllium, Be
铜
镍

材料描述		测试方法
RMWA Class	3