3M 7864 Thermal Transfer Polyester Label Material

3M™ Thermal Transfer Polyester Label Materials are thin profile, gloss polyester label stocks that offer excellent durability and moisture resistance. These label materials utilize 3M™ Adhesive 400 which is designed to offer good peel strength to a variety of surfaces, as well as, excellent clarity and UV resistance.

Information provided by 3M

物理性能	额定值 (公制)	额定值 (英制)	测试方法
厚度	microns	mil	Adhesive
	microns	mil	Facestock
	microns	mil	Liner

机械性能	额定值 (公制)	额定值 (英制)	测试方法
剥离强度	kN/m	pli	Stainless Steel, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330
	kN/m	pli	Stainless Steel, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
	kN/m	pli	LD Polyethylene, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330
	kN/m	pli	Stainless Steel, 180° Peel, Conditioned for 3 days at RT; ASTM D3330
	kN/m	pli	Stainless Steel, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
	kN/m	pli	LD Polyethylene, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330
	kN/m	pli	HD Polyethylene, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330
	kN/m	pli	LD Polyethylene, 90° Peel, Conditioned for 3 days at RT; ASTM D3330
	kN/m	pli	LD Polyethylene, 180° Peel, Conditioned for 3 days at RT; ASTM D3330
	kN/m	pli	Stainless Steel, 90° Peel, Conditioned for 3 days at RT; ASTM D3330
	kN/m	pli	LD Polyethylene, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330
	kN/m	pli	HD Polyethylene, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
	kN/m	pli	Stainless Steel, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330
	kN/m	pli	LD Polyethylene, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
	kN/m	pli	LD Polyethylene, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
	kN/m	pli	Glass, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330
	kN/m	pli	LD Polyethylene, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330
	kN/m	pli	Glass, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
	kN/m	pli	Stainless Steel, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330
	kN/m	pli	HD Polyethylene, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330
	kN/m	pli	Glass, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330
	kN/m	pli	Polypropylene, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330
	kN/m	pli	Glass, 90° Peel, Conditioned for 3 days at RT; ASTM D3330
	kN/m	pli	Polypropylene, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330
	kN/m	pli	Polypropylene, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330
	kN/m	pli	Polypropylene, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330
	kN/m	pli	Glass, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
	kN/m	pli	Stainless Steel, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330
	kN/m	pli	Glass, 180° Peel, Conditioned for 3 days at RT; ASTM D3330
	kN/m	pli	Glass, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330
	kN/m	pli	Polycarbonate 90° Peel, Conditioned for 3 days at RT; ASTM D3330
	kN/m	pli	Glass, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330
	kN/m	pli	Polycarbonate 180° Peel, Initial, 10 min dwell at RT; ASTM D3330
	kN/m	pli	Polycarbonate 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
	kN/m	pli	Polypropylene, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
	kN/m	pli	Polypropylene, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
	kN/m	pli	Polypropylene, 90° Peel, Conditioned for 3 days at RT; ASTM D3330
	kN/m	pli	Polycarbonate 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330
	kN/m	pli	HD Polyethylene, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330
	kN/m	pli	Polypropylene, 180° Peel, Conditioned for 3 days at RT; ASTM D3330
	kN/m	pli	HD Polyethylene, 180° Peel, Conditioned for 3 days at RT; ASTM D3330
	kN/m	pli	HD Polyethylene, 90° Peel, Conditioned for 3 days at RT; ASTM D3330
	kN/m	pli	Polycarbonate 180° Peel, Conditioned for 3 days at RT; ASTM D3330
	kN/m	pli	Polycarbonate 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330
	kN/m	pli	HD Polyethylene, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
	kN/m	pli	HD Polyethylene, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330
	kN/m	pli	Polycarbonate 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330

热性能	额定值 (公制)	额定值 (英制)	测试方法
最高工作温度, Air	°C	°F	Service
最低工作温度, Air	°C	°F	Service
	°C	°F	Application

加工性能	额定值 (公制)	额定值 (英制)	测试方法
保质期	Month	Month

材料描述		测试方法
粘合剂类型	400 Acrylic
Liner	55# Densified Kraft