Information provided by Georgia Gulf
Georgia Gulf became Axiall Corporation in 2013.| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | g/cc | g/cc | Natural; ASTM D-792 |
| 线性成型收缩率 | cm/cm | in/in | ASTM D-955 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(屈服) | MPa | psi | ASTM D-638 |
| 拉伸模量 | GPa | ksi | ASTM D-638 |
| 悬壁梁缺口冲击强度 | J/cm @Thickness 3.17 mm, Temperature -40.0 °C | ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F | ASTM D-256 |
| J/cm @Thickness 3.17 mm, Temperature -20.0 °C | ft-lb/in @Thickness 0.125 in, Temperature -4.00 °F | ASTM D-256 | |
| J/cm @Thickness 3.17 mm, Temperature 0.000 °C | ft-lb/in @Thickness 0.125 in, Temperature 32.0 °F | ASTM D-256 | |
| J/cm @Thickness 3.17 mm, Temperature 23.0 °C | ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D-256 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度(0.46 MPa) | °C | °F | unannealed; ASTM D-648 |
| °C | °F | annealed; ASTM D-648 | |
| 载荷下热变形温度(1.8 MPa) | °C | °F | unannealed; ASTM D-648 |
| °C | °F | annealed; ASTM D-648 | |
| 维卡软化温度 | °C | °F | annealed; ASTM D-1525A |
| UL RTI | °C | °F | UL-746B |
| UL RTI，机械冲击 | °C | °F | UL-746B |
| UL RTI，机械无冲击 | °C | °F | UL-746B |
| 可燃性(UL94) | @Thickness 1.60 mm | @Thickness 0.0630 in | |
| @Thickness 3.00 mm | @Thickness 0.118 in |
| 材料描述 | 测试方法 | |
|---|---|---|
| Cell Classification | 14002123 | ASTM D-4216 |
| Cell Classification, ASTM D-1784 | 15233 |