High performance thermoplastic material, 30% carbon fibre reinforced PolyEtherKetoneEtherKetoneKetone (PEKEKK), semi crystalline, granules for injection moulding, standard flow, colour black.
Typical Application Areas:
Applications for higher strength and stiffness at elevated temperatures in a static or dynamic system. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.
Information Provided by VICTREX®| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | Crystalline; ISO 1183 |
| 饱和吸水率 | @Temperature 100 °C | @Temperature 212 °F | immersion; ISO 62-1 |
| 粘度 | cP @Temperature 420 °C | cP @Temperature 788 °F | melt; ISO 11443 |
| 线性成型收缩率,Flow | cm/cm | in/in | 360°C nozzle, 160°C tool; ISO 294-4 |
| 线性成型收缩率，横向 | cm/cm | in/in | 415°C nozzle, 210°C tool; ISO 294-4 |
| Spiral Flow | cm @Thickness 1.00 mm | in @Thickness 0.0394 in | 415°C nozzle, 210°C tool |
| cm @Thickness 3.00 mm | in @Thickness 0.118 in | 415°C nozzle, 210°C tool |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | ISO 868 | ||
| 抗张强度(断裂) | MPa @Temperature 275 °C | psi @Temperature 527 °F | ISO 527 |
| MPa @Temperature 175 °C | psi @Temperature 347 °F | ISO 527 | |
| MPa @Temperature 125 °C | psi @Temperature 257 °F | ISO 527 | |
| MPa @Temperature 23.0 °C | psi @Temperature 73.4 °F | ISO 527 | |
| 伸长率 (断裂) | @Temperature 23.0 °C | @Temperature 73.4 °F | ISO 527 |
| 拉伸模量 | GPa @Temperature 23.0 °C | ksi @Temperature 73.4 °F | ISO 527 |
| 弯曲强度 | MPa @Temperature 275 °C | psi @Temperature 527 °F | ISO 178 |
| MPa @Temperature 175 °C | psi @Temperature 347 °F | ISO 178 | |
| MPa @Temperature 125 °C | psi @Temperature 257 °F | ISO 178 | |
| MPa @Temperature 23.0 °C | psi @Temperature 73.4 °F | ISO 178 | |
| 弯曲模量 | GPa @Temperature 23.0 °C | ksi @Temperature 73.4 °F | ISO 178 |
| 抗压强度 | MPa @Temperature 250 °C | psi @Temperature 482 °F | ISO 604 |
| MPa @Temperature 200 °C | psi @Temperature 392 °F | ISO 604 | |
| MPa @Temperature 120 °C | psi @Temperature 248 °F | ISO 604 | |
| MPa @Temperature 23.0 °C | psi @Temperature 73.4 °F | ISO 604 | |
| 悬壁梁缺口冲击强度 | kJ/m² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | ISO 180/A |
| 悬壁梁无缺口冲击强度 | kJ/m² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | ISO 180/U |
| 简支梁无缺口冲击强度 | J/cm² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | ISO 179/1U |
| 简支梁缺口冲击强度 | J/cm² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 1V; ASTM D4496 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线性热膨胀系数 | µm/m-°C @Temperature <=162 °C | µin/in-°F @Temperature <=324 °F | Average below Tg; ISO 11359 |
| µm/m-°C @Temperature >=162 °C | µin/in-°F @Temperature >=324 °F | Average above Tg; ISO 11359 | |
| 线形热膨胀系数 - 流动 | µm/m-°C @Temperature <=162 °C | µin/in-°F @Temperature <=324 °F | Below Tg; ISO 11359 |
| µm/m-°C @Temperature >=162 °C | µin/in-°F @Temperature >=324 °F | Above Tg; ISO 11359 | |
| 导热系数 | W/m-K | BTU-in/hr-ft²-°F | Average; ISO 22007-4 |
| W/m-K | BTU-in/hr-ft²-°F | Along flow; ISO 22007-4 | |
| 熔融温度 | °C | °F | ISO 11357 |
| 载荷下热变形温度(1.8 MPa) | °C | °F | ISO 75-f |
| 玻璃化转变温度，Tg | °C | °F | Onset; ISO 11357 |
| °C | °F | Midpoint; ISO 11357 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工温度 | <= °C | <= °F | Hopper Temperature |
| 射嘴温度 | °C | °F | |
| 模具温度 | °C | °F | |
| 干燥温度 | °C @Time 21600 sec | °F @Time 6.00 hour | |
| °C @Time 10800 sec | °F @Time 3.00 hour |