Resin Type: enhanced linear low density polyethylene, slip, antiblock and processing aid additives
Characteristics: superior dart impact, optical, hot-tack and heat seal properties, good drawdown, can be used straight or blended with LDPE or HDPE
Applications: thick or thin film applications where superior toughness and abuse resistance, hot-tack and heat-seal, and optical properties are critical
Natural Color
Slip: 0 ppm
Antiblock: 0 ppm.
Recommended processing conditions: 6.35 cm extruder. 24:1 screw L/D ratio. 0.203 cm die opening. Melt temperature 232°C. Blow up ratio 2.5:1. Output rate 8.0 lb/hr/in die cir.
Hot-Tack Initiation Temperature: 73°C
Ultimate Hot-Tack Strength: 4.2 N
Heat Seal Initiation Temperature at 0.5 lb.: 92°C
Ultimate Heat Seal Strength: 10.7 N.
Film properties based on thickness of 0.0318 mm.
Information provided by Chevron Phillips Chemical Company.
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | ASTM D4883 |
| 熔体流动速率 | g/10 min | g/10 min | Condition E; ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 断裂伸长率，MD | ASTM D882 | ||
| 断裂伸长率，TD | ASTM D882 | ||
| 割线模量(MD) | GPa | ksi | ASTM D882 |
| 割线模量(TD) | GPa | ksi | ASTM D882 |
| 摩擦系数 | ASTM D1894 | ||
| 埃尔曼多夫抗撕强度(MD) | g/micron | g/mil | ASTM D1922 |
| 埃尔曼多夫抗撕强度(TD) | g/micron | g/mil | ASTM D1922 |
| 落锤 | g/micron | g/mil | F-50 at 26 in.; ASTM D1709 |
| 落锤试验 | g | lb | F-50 at 26 in.; ASTM D1709 |
| 抗张强度(MD : 断裂) | MPa | psi | ASTM D882 |
| 抗张强度(TD : 断裂) | MPa | psi | ASTM D882 |
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 雾度 | ASTM D2457 | ||
| 光泽度 | 60°; ASTM D 2457 | ||
| 45°; ASTM D 2457 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | °C | °F |