| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | g/cc | g/cc | ASTM D792 |
| 密度 | g/cc | lb/in³ | ASTM D792 |
| g/cc | lb/in³ | ISO 1183 | |
| 吸水率 | @Time 86400 sec | @Time 24.0 hour | ASTM D570 |
| 平衡吸湿 | ASTM D570 | ||
| @Temperature 100 °C | @Temperature 212 °F | ASTM D570 | |
| 线性成型收缩率,Flow | cm/cm @Thickness 3.20 mm | in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | g/10 min @Load 1.20 kg, Temperature 300 °C | g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
| 化合物熔体指数 | g/10 min @Load 1.20 kg, Temperature 300 °C | g/10 min @Load 2.65 lb, Temperature 572 °F | MVR [cm^3/10 min]; ISO 1133 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（M 级） | ASTM D785 | ||
| 洛氏硬度（R 级） | ASTM D785 | ||
| 硬度，H358/30 | MPa | psi | ISO 2039-1 |
| 抗张强度(断裂) | MPa | psi | 50 mm/min; ISO 527 |
| MPa | psi | Type I, 50 mm/min; ASTM D638 | |
| 抗张强度(屈服) | MPa | psi | Type I, 50 mm/min; ASTM D638 |
| MPa | psi | 50 mm/min; ISO 527 | |
| 伸长率 (断裂) | 50 mm/min; ISO 527 | ||
| Type I, 50 mm/min; ASTM D638 | |||
| 屈服伸长率 | Type I, 50 mm/min; ASTM D638 | ||
| 50 mm/min; ISO 527 | |||
| 拉伸模量 | GPa | ksi | 1 mm/min; ISO 527 |
| GPa | ksi | 50 mm/min; ASTM D638 | |
| 弯曲强度 | MPa | psi | 2 mm/min; ISO 178 |
| MPa | psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 弯曲模量 | GPa | ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| GPa | ksi | 2 mm/min; ISO 178 | |
| 悬壁梁缺口冲击强度 | J/cm | ft-lb/in | colors; ASTM D256 |
| J/cm | ft-lb/in | natural, tints; ASTM D256 | |
| 悬壁梁无缺口冲击强度 | J/cm | ft-lb/in | ASTM D4812 |
| 悬壁梁缺口冲击强度 | kJ/m² | ft-lb/in² | 80*10*4; ISO 180/1A |
| kJ/m² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| 悬壁梁无缺口冲击强度 | 80*10*4; ISO 180/1U | ||
| @Temperature -30.0 °C | @Temperature -22.0 °F | 80*10*4; ISO 180/1U | |
| 简支梁缺口冲击强度 | J/cm² | ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| J/cm² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| 拉伸冲击强度 | kJ/m² | ft-lb/in² | Type S; ASTM D1822 |
| 落锤总能量 | J | ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| J | ft-lb | ASTM D3029 | |
| 泰伯磨损，毫克/1000次 | CS-17, 1 kg; ASTM D1044 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | >= ohm-cm | >= ohm-cm | IEC 60093 |
| >= ohm-cm | >= ohm-cm | ASTM D257 | |
| 表面电阻 | >= ohm | >= ohm | ROA; IEC 60093 |
| 介电常数 | @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | IEC 60250 |
| @Frequency 50.0 - 60.0 Hz | @Frequency 50.0 - 60.0 Hz | IEC 60250 | |
| @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | ASTM D150 | |
| @Frequency 50.0 - 60.0 Hz | @Frequency 50.0 - 60.0 Hz | ASTM D150 | |
| 介电强度 | kV/mm @Thickness 3.20 mm | kV/in @Thickness 0.126 in | in air; ASTM D149 |
| kV/mm @Thickness 3.20 mm | kV/in @Thickness 0.126 in | in oil; IEC 60243-1 | |
| 耗散因数 | @Frequency 50.0 - 60.0 Hz | @Frequency 50.0 - 60.0 Hz | ASTM D150 |
| @Frequency 50.0 - 60.0 Hz | @Frequency 50.0 - 60.0 Hz | IEC 60250 | |
| @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | IEC 60250 | |
| @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | ASTM D150 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | µm/m-°C @Temperature -40.0 - 95.0 °C | µin/in-°F @Temperature -40.0 - 203 °F | ASTM E 831 |
| µm/m-°C @Temperature 23.0 - 80.0 °C | µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
| 比热容 | J/g-°C | BTU/lb-°F | ASTM C351 |
| 导热系数 | W/m-K | BTU-in/hr-ft²-°F | ASTM C177 |
| W/m-K | BTU-in/hr-ft²-°F | ISO 8302 | |
| 载荷下热变形温度(0.46 MPa) | °C | °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| °C @Thickness 6.40 mm | °F @Thickness 0.252 in | unannealed; ASTM D648 | |
| 载荷下热变形温度(1.8 MPa) | °C | °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| °C @Thickness 6.40 mm | °F @Thickness 0.252 in | unannealed; ASTM D648 | |
| 维卡软化温度 | °C | °F | Rate B/50; ISO 306 |
| °C | °F | Rate B/120; ISO 306 | |
| 极限氧指数 | ISO 4589 |
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 折射率 | ASTM D542 | ||
| 雾度 | @Thickness 2.54 mm | @Thickness 0.100 in | ASTM D1003 |
| Transmission, Visible | 2.54 mm; ASTM D1003 |
| 材料描述 | 测试方法 | |
|---|---|---|
| 球压试验，125°C+/-2℃ | PASSES | IEC 60695-10-2 |
| Specific Volume | 0.83cm^3/g | ASTM D792 |