| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | Base Resin; ASTM D1505 |
| 熔体流动速率 | g/10 min @Load 2.16 kg, Temperature 190 °C | g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1283/L |
| g/10 min @Load 21.6 kg, Temperature 190 °C | g/10 min @Load 47.6 lb, Temperature 374 °F | Flow@21.6kg/Flow@2.16kg ratio < 30; ASTM D1283 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(MD : 屈服) | >= MPa | >= psi | ASTM D882 |
| 抗张强度(TD : 屈服) | >= MPa | >= psi | ASTM D882 |
| 断裂伸长率，MD | ASTM D882 | ||
| 断裂伸长率，TD | ASTM D882 | ||
| 拉伸模量 | >= GPa | >= ksi | 2% sec, MD; ASTM D882 |
| >= GPa | >= ksi | 2% sec, TD; ASTM D882 | |
| 埃尔曼多夫抗撕强度(MD) | >= g/micron | >= g/mil | ASTM D1922 |
| 埃尔曼多夫抗撕强度(TD) | >= g/micron | >= g/mil | ASTM 1922 |
| 落锤试验 | >= g | >= lb | ASTM D1709 |
| 材料描述 | 测试方法 | |
|---|---|---|
| Gel Content (pcs./m²) | 0 | > 1mm |
| 245 | (0.2-0.5)mm | |
| 250 | > 0.2mm (totally) | |
| 5 | (0.5-1.0)mm |