3M Scotch-Weld™ EZ250150 Polyurethane Reactive (PUR) Easy 250 Wood Adhesive

3M™ Scotch-Weld™ Polyurethane Reactive (PUR) Easy 250 Wood Adhesive is 100% solid, warm temperature applied, moisture curing urethanes. This product bonds a wide variety of plastics and wood to themselves and to metal glass. Long open and set time ideal for bonding a wide variety of substrates including wood, plastics and also bonds aluminum glass to plastics and wood.

Information provided by 3M

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	g/cc	lb/in³
布氏粘度	cP	cP	Thermosel using spindle #27

机械性能	额定值 (公制)	额定值 (英制)	测试方法
肖氏硬度 (邵氏 D)
抗张强度(断裂)	MPa	psi	ASTM D638 Die C
伸长率 (断裂)			ASTM D638 Die C
抗剪强度	MPa @Temperature 82.0 °C	psi @Temperature 180 °F	Overlap, PVC
	MPa @Temperature 82.0 °C	psi @Temperature 180 °F	Overlap, Maple
	MPa @Temperature 23.0 °C	psi @Temperature 73.4 °F	Overlap, ABS, Substrate Failure
	MPa @Temperature 23.0 °C	psi @Temperature 73.4 °F	Overlap, Polyacrylic, Substrate Failure
	MPa @Temperature 23.0 °C	psi @Temperature 73.4 °F	Overlap, Polycarbonate
	MPa @Temperature 23.0 °C	psi @Temperature 73.4 °F	Overlap, Maple
	MPa @Temperature 23.0 °C	psi @Temperature 73.4 °F	Overlap, PVC
	MPa @Time Error in fixSigDigits: @digits must be between 1 a sec	psi @Time Error in fixSigDigits: @digits must be between 1 a hour	Overlap, PVC
	MPa @Time Error in fixSigDigits: @digits must be between 1 a sec	psi @Time Error in fixSigDigits: @digits must be between 1 a hour	Overlap, Maple
	MPa @Time 3600 sec	psi @Time 1.00 hour	Overlap, PVC
	MPa @Time 3600 sec	psi @Time 1.00 hour	Overlap, Maple
	MPa @Time 605000 sec	psi @Time 168 hour	Overlap, Maple
	MPa @Time 259000 sec	psi @Time 72.0 hour	Overlap, Maple
	MPa @Time 86400 sec	psi @Time 24.0 hour	Overlap, Maple
	MPa @Time 86400 sec	psi @Time 24.0 hour	Overlap, PVC
	MPa @Time 259000 sec	psi @Time 72.0 hour	Overlap, PVC
	MPa @Time 605000 sec	psi @Time 168 hour	Overlap, PVC
剥离强度	kN/m	pli	180°, Polyacrylic
	kN/m	pli	180°, Aluminum
	kN/m	pli	180°, ABS
	kN/m	pli	180°, Glass
	kN/m	pli	180°, PVC, Cotton duck failed during testing
	kN/m	pli	180°, Polycarbonate, Cotton duck failed during testing

热性能	额定值 (公制)	额定值 (英制)	测试方法
最高工作温度, Air	°C	°F

加工性能	额定值 (公制)	额定值 (英制)	测试方法
固化时间	min	hour	Set Time

材料描述		测试方法
外观	white/off-white