Advanced Polymer Alloys DuraGrip™ 6170 BK Melt Processable Elastomer

DuraGrip™ 6170BK is designed to be a special purpose Melt Processable Elastomer (MPE) that is easy to use in injection molding and extrusion processes. DGR 6170BK has an excellent soft touch feel and will Bond to Nylon, ABS, PC, PC/ABS. DuraGrip™ 6100 series is hygroscopic and requires drying prior to use.

Information provided by Advanced Polymer Alloys

物理性能	额定值 (公制)	额定值 (英制)	测试方法
比重	g/cc	g/cc	ASTM D471; ISO 2781
粘度	cP @Shear Rate 300 1/s, Temperature 190 °C	cP @Shear Rate 300 1/s, Temperature 374 °F	ASTM D3835
线性成型收缩率	cm/cm	in/in
	cm/cm	in/in
线性成型收缩率，横向	cm/cm	in/in
	cm/cm	in/in

机械性能	额定值 (公制)	额定值 (英制)	测试方法
肖氏硬度 (邵氏 A)			Time of 5 seconds; ASTM D2240; ISO 48
极限抗拉强度	MPa	psi	ASTM D412; ISO 37
	MPa	psi	After 7 days at 70°C; ASTM D412 ISO 37
	MPa	psi	After 7 days at 100oC; ASTM D412 ISO 37
伸长率 (断裂)			ASTM D412; ISO 37
			After 7 days at 70°C; ASTM D412 ISO 37
			After 7 days at 100°C; ASTM D412 ISO 37
弹性模量	GPa	ksi	After 7 days at 100°C; ASTM D412 ISO 37
	GPa	ksi	After 7 days at 70°C; ASTM D412 ISO 37
100% 模量	GPa	ksi	ASTM D412; ISO 37
Graves Tear Strength	kN/m @Temperature 23.9 °C	pli @Temperature 75.0 °F	Die C; ASTM D624
泰伯磨损，毫克/1000次			Cs-17 Wheel, 1000 g Load; ASTM D3389
永久压缩			After 22 Hr at 75°F (24°C); ASTM D395; ISO 815
	@Temperature 70.0 °C	@Temperature 158 °F	22 hrs.; ASTM D395; ISO 815
	@Temperature 100 °C	@Temperature 212 °F	22 hrs.; ASTM D395; ISO 815
Tensile Set			100% Tension; ASTM D412

热性能	额定值 (公制)	额定值 (英制)	测试方法
脆化温度	°C	°F	ASTM D746; ISO 812

加工性能	额定值 (公制)	额定值 (英制)	测试方法
加工温度	°C	°F
料筒后部温度	°C	°F
料筒中部温度	°C	°F
料筒前部温度	°C	°F
射嘴温度	°C	°F
加工（熔体）温度	°C	°F
模具温度	°C	°F
注射压力	MPa	psi
Cycle Time - Injection	sec	sec	boost
螺杆转速	rpm	rpm
固化时间	min	hour	Cooling Time

材料描述		测试方法
Fluid Resistance - Volume Change, % (ASTM D471)	1	After 7 Days in Water at 212°F (100°C)
	42	After 7 Days in IRM 903 Oil No.3 at 212°F (100°C)
	49	After 7 Days in ASTM Ref. Fuel No. B at 75°F (24°C)
	5	After 7 Days in ASTM Oil No.1 at 212°F (100°C)