Typical Applications: Spiral tubing, pneumatic tubing, round and v-belting, technical moldings, e.g. bushes, dust caps, seals, blow molding bellows, and mining screens.
Note: Quoted results are from measurements on injection molded test platens, post tempered for 20 hours at 100°C
Information provided by BASF| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | ISO 1183-1-A |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 A) | ISO 868 | ||
| 抗张强度 | MPa | psi | after storage in water at 80°C for 42 days; ISO 37 |
| MPa | psi | ISO 37 | |
| MPa @Strain 20.0 % | psi @Strain 20.0 % | ISO 37 | |
| MPa @Strain 100 % | psi @Strain 100 % | ISO 37 | |
| MPa @Strain 300 % | psi @Strain 300 % | ISO 37 | |
| 伸长率 (断裂) | ISO 37 | ||
| after storage in water at 80°C for 42 days; ISO 37 | |||
| 简支梁缺口冲击强度 | @Temperature -30.0 °C | @Temperature -22.0 °F | DIN EN ISO 179 |
| @Temperature 23.0 °C | @Temperature 73.4 °F | DIN EN ISO 179 | |
| 撕裂强度 | kN/m | pli | DIN ISO 34-1/Bb |
| 磨损 | [mm<sup>3</sup>; ISO 4649 | ||
| 压缩永久变形 | @Temperature 23.0 °C | @Temperature 73.4 °F | ISO 815 |
| @Temperature 70.0 °C | @Temperature 158 °F | ISO 815 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工温度 | °C | °F | Extrusion |
| °C | °F | Injection molding | |
| 模具温度 | °C | °F |
| 材料描述 | 测试方法 | |
|---|---|---|
| 商业地位 | North America | |
| Primary Processing Technique | Injection molding and Extrusion |