| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | g/cc | g/cc | ASTM D792 |
| 线性成型收缩率,Flow | cm/cm @Thickness 3.20 mm | in/in @Thickness 0.126 in | ASTM D955 |
| 线性成型收缩率，横向 | cm/cm @Thickness 3.20 mm | in/in @Thickness 0.126 in | ASTM D955 |
| 熔体流动速率 | g/10 min @Load 2.16 kg, Temperature 250 °C | g/10 min @Load 4.76 lb, Temperature 482 °F | ASTM D1238 |
| g/10 min @Load 10.0 kg, Temperature 220 °C | g/10 min @Load 22.0 lb, Temperature 428 °F | ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | ASTM D785 | ||
| 抗张强度(断裂) | MPa | psi | 5 mm/min; ASTM D638 |
| 抗张强度(屈服) | MPa | psi | 5 mm/min; ASTM D638 |
| 伸长率 (断裂) | 5 mm/min; ASTM D638 | ||
| 拉伸模量 | GPa | ksi | 5 mm/min; ASTM D638 |
| 弯曲强度 | MPa | psi | 2.8 mm/min; ASTM D790 |
| 弯曲模量 | GPa | ksi | 2.8 mm/min; ASTM D790 |
| 悬壁梁缺口冲击强度 | J/cm @Thickness 3.17 mm, Temperature -30.0 °C | ft-lb/in @Thickness 0.125 in, Temperature -22.0 °F | ASTM D256 |
| J/cm @Thickness 6.35 mm, Temperature -30.0 °C | ft-lb/in @Thickness 0.250 in, Temperature -22.0 °F | ASTM D256 | |
| J/cm @Thickness 6.35 mm, Temperature 23.0 °C | ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | ASTM D256 | |
| J/cm @Thickness 3.17 mm, Temperature 23.0 °C | ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D256 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度(0.46 MPa) | °C @Thickness 6.40 mm | °F @Thickness 0.252 in | ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | °C @Thickness 6.40 mm | °F @Thickness 0.252 in | ASTM D648 |
| 维卡软化温度 | °C | °F | B/50; ISO R306 |
| °C | °F | B/120; ISO R306 |
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| Yellow Index | @Thickness 31.2 mm | @Thickness 1.23 in | ASTM D1925 |