POTICON ONN30B

The Poticon series features a potassium titanate micro-filler compounded in thermoplastic resins to provide outstanding micro-reinforcement and dimensional stability. The excellent surface smoothness of these compounds limits friction toward opposing materials, reducing wear and allowing for greaseless applications. Moreover, as Poticon diminishes damage toward the mold and metal die and offers excellent recyclability, it also decreases processing costs.

Advantages

• Microscopic reinforcement

• Superior friction sliding and wear reduction

• Excellent dimensional accuracy and surface smoothness

• Highly recyclable

Applications

• Automotive Parts (gears, bearings)

• LED Reflectors

• Watch Parts (gears, ground plane)

• Camera (image stabilization parts)

• Sliding Parts (gears, wheel bearing)

• Camera Module Parts

• Motor Parts (cog-wheels, bearings)

ONN30B Property: General-purpose

基本信息
特性	High Dimensional Stability 低摩擦系数 可回收材料 通用
用途	LEDs 齿轮 汽车领域的应用 通用 相机应用 轴承
加工方法	注射成型

物理性能	额定值	单位制	测试方法
比重		g/cm³	ASTM D792
收缩率
流动		%
横向流动		%
吸水率 (平衡)		%	ASTM D570

硬度	额定值	单位制	测试方法
洛氏硬度 (M 级)			ASTM D785

机械性能	额定值	单位制	测试方法
抗张强度		MPa	ASTM D638
伸长率 (断裂)		%	ASTM D638
弯曲模量		MPa	ASTM D790
弯曲强度		MPa	ASTM D790
摩擦系数 (与钢 - 动态)
磨损量
-- 1		10^-3 mm³/N·km
of counterpart 2		10^-3 mm³/N·km

热性能	额定值	单位制	测试方法
Heat Distortion		°C	ASTM D648

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度		J/m	ASTM D256

热性能	额定值	单位制	测试方法
线形热膨胀系数 - 流动		cm/cm/°C	ASTM D696

注射	额定值	单位制
加工（熔体）温度		°C
模具温度		°C
注塑压力		MPa

备注
1 .	Surface pressure: 1MPa
2 .	Slipping velocity: 0.3m/sec