Braskem PE LL5405S

LL5405S is a Linear Low Density Polyethylene (LLDPE) developed for blown film extrusion. Films obtained with this product show a good processing performance balanced with good mechanical properties as well as processability. Very low gel amount.

Additive:
Antiblocking ­ High
Slip - High

Applications:
LLDPE and HDPE blends, films with low thickness for general use, bags for waste, special bags for water and protection of clothes.

Process:
Blown film extrusion.

基本信息
添加剂	高光滑性 高抗结块性
特性	低速凝固晶点 高光滑性 高抗结块性 可加工性，良好
用途	Blown Film 薄膜 袋子 混合
机构评级	FDA 21 CFR 177.1520
加工方法	吹塑薄膜

物理性能	额定值	单位制	测试方法
比重		g/cm³	ASTM D792
熔流率（熔体流动速率） (190°C/2.16 kg)		g/10 min	ASTM D1238

机械性能	额定值	单位制	测试方法
摩擦系数 (吹塑薄膜)			ASTM D1894

薄膜	额定值	单位制	测试方法
抗张强度			ASTM D882
MD : 断裂, 40 µm, 吹塑薄膜		MPa	ASTM D882
TD : 断裂, 40 µm, 吹塑薄膜		MPa	ASTM D882
伸长率			ASTM D882
MD : 断裂, 40 µm, 吹塑薄膜		%	ASTM D882
TD : 断裂, 40 µm, 吹塑薄膜		%	ASTM D882
弯曲模量			ASTM D790
1% Secant, MD : 40 µm, Blown Film		MPa	ASTM D790
1% Secant, TD : 40 µm, Blown Film		MPa	ASTM D790
落锤冲击 (40 µm, 吹塑薄膜)		g	ASTM D1709
埃尔曼多夫抗撕强度			ASTM D1922
MD : 40 µm, 吹塑薄膜		g	ASTM D1922
TD : 40 µm, 吹塑薄膜		g	ASTM D1922

光学性能	额定值	单位制	测试方法
光泽度			ASTM D2457
45°, 40.0 µm, 吹塑薄膜			ASTM D2457
60°, 40.0 µm, 吹塑薄膜			ASTM D2457
雾度 (40.0 µm, 吹塑薄膜)		%	ASTM D1003

补充信息	额定值	单位制	测试方法
Blocking 1(40.0 µm)		g/100 cm²	ASTM D3354

备注
1 .	Blown Film