AEI SX546:CM497CD and SX546:CM493CD

125°C rated silane crosslinkable polyethylene for low voltage power cable insulation

This is a silane crosslinkable polyethylene compound for insulation of power cables and is especially designed for operation temperatures up to 125°C. It possesses outstanding extrusion properties with low scorch characteristics. High output rates can be achieved with minimum point and die drool.

The graft component SX546 is mixed with a crosslinking catalyst masterbatch CM497CD or CM493CD generally in the ratio 95:5. This compound can also be cured at ambient temperatures and has a nominal melt index of 1.2.

基本信息
特性	可交联
用途	低压绝缘 电线电缆应用
机构评级	EC 1907/2006 (REACH)
RoHS 合规性	RoHS 合规
形式	粒子
加工方法	挤出

物理性能	额定值	单位制	测试方法
密度		g/cm³	BS 2782 620A

机械性能	额定值	单位制	测试方法
拉伸应力		MPa	IEC 60811-1-1
拉伸应变 (断裂)		%	IEC 60811-1-1

老化	额定值	单位制	测试方法
拉伸强度的变化率			IEC 60811-1-2
125°C, 3000 hr		%	IEC 60811-1-2
155°C, 240 hr		%	IEC 60811-1-2
断裂时拉伸应力变化			IEC 60811-1-2
125°C, 3000 hr		%	IEC 60811-1-2
155°C, 240 hr		%	IEC 60811-1-2

热性能	额定值	单位制	测试方法
冷弯曲 (-70°C)			IEC 60811-1-4
热固性 1			IEC 60811-2-1
Elongation under load, 20N/cm² : 200°C		%	IEC 60811-2-1
Permanent elongation after cooling		%	IEC 60811-2-1

电气性能	额定值	单位制	测试方法
功率因数 - 50Hz (23°C)			IEC 60250

补充信息	额定值	单位制
Cure Time - <100% Hot Set 2
800.0 µm		hr
1.50 mm		hr

挤出	额定值	单位制
头部温度		°C

电气性能	额定值	单位制	测试方法
体积电阻率 (20°C)		ohms·cm	IEC 60502
介电强度 (20°C)		kV/mm	IEC 60243-1
相对电容率 (23°C, 50 Hz)			IEC 60250

挤出	额定值	单位制
料筒1区温度		°C
料筒2区温度		°C
料筒3区温度		°C
料筒4区温度		°C
口模温度		°C

挤压说明
Most modern thermoplastic extruders will process the SX546:CM497CDsystem, particularly if a screw suitable for the extrusion of polyethylene is available.

备注
1 .	Cure assessment by hot set test (forced cured at 80°C in water)
2 .	Cure assessment (ambient cure at 20°C and 50% humidity)