Menzolit® SMC 0170

聚酯,TS

Menzolit Ltd (UK)

产品说明

Menzolit® SMC 0170 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens.

Menzolit® SMC 0170 is a general purpose SMC for applications in the field of electrical industry. Typical applications are housings, covers, wire distribution boxes and metering cabinets. The material meets the demands of DIN 16913 and is classified as type 832 (832.5) regarding mechanical properties. The flammability meets the demands of standard UL 94 category HB. The glass content is on a level that combines good mouldability with good mechanical properties regarding strength and stiffness.
基本信息
填料/增强材料
  • 玻璃\矿物, 32% 填料按重量
特性
  • 低烟度
  • 刚性,良好
  • 良好的成型性能
  • 良好的强度
  • 耐热性,高
  • 通用
  • 无卤
  • 阻燃性
用途
  • 电气/电子应用领域
  • 通用
  • 外壳
机构评级
  • DIN 16913 type 832.5
外观
  • 可用颜色
形式
  • SMC - 片状模塑料
加工方法
  • 压缩模塑
部件标识代码 (ISO 11469)
  • >UP-(MD+GF)72
物理性能额定值单位制测试方法
密度 g/cm³ISO 1183
收缩率
    -- 1%DIN 53464
    -- %ISO 2577
吸水率 (饱和, 23°C)%ISO 62
机械性能额定值单位制测试方法
拉伸模量 (模压成型)MPaISO 527-2
拉伸应力 (屈服, 模压成型)MPaISO 527-2
弯曲模量 (模压成型)MPaISO 178
弯曲应力 (模压成型)MPaISO 178
冲击性能额定值单位制测试方法
简支梁缺口冲击强度 (模压成型)kJ/m²ISO 179
热性能额定值单位制测试方法
热变形温度 (1.8 MPa, 未退火)°CISO 75-2/A
连续使用温度 °C内部方法
玻璃转化温度 °CDSC
线形热膨胀系数 - 流动 cm/cm/°CISO 11359-2
电气性能额定值单位制测试方法
表面电阻率 ohmsIEC 60093
体积电阻率 ohms·cmIEC 60093
漏电起痕指数 VIEC 60112
可燃性额定值单位制测试方法
UL 阻燃等级 (2.00 mm)UL 94
热灯丝点火温度 °CIEC 60695-2-13
极限氧指数 %ISO 4589-2
补充信息额定值测试方法
Glow Bar IEC 60707-3
注射额定值单位制
模具温度 °C
注塑压力 MPa
备注
1 .Post Molding Shrinkage
Copyright © souwuxing.com All Rights Reserved. 归 搜聚信息科技公司 所有
此数据表中的信息由 搜聚 从该材料的生产商处获得。搜聚 尽最大努力确保此数据的准确性。 但是 搜聚 对这些数据值不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。