| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | g/cc | g/cc | ASTM D792 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | 15 sec; ASTM D2240 | ||
| 抗张强度(屈服) | MPa | psi | Type I, 5.1 mm/min; ASTM D638 |
| 拉伸模量 | GPa | ksi | Type I, 5.1 mm/min; ASTM D638 |
| 弯曲强度 | MPa | psi | ASTM D790 |
| 弯曲模量 | GPa | ksi | ASTM D790 |
| 悬壁梁缺口冲击强度 | J/cm @Thickness 3.18 mm, Temperature 23.0 °C | ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Compression Molded; ASTM D256A |
| Dart Drop Total Energy | J/cm @Temperature 23.0 °C | ft-lb/mil @Temperature 73.4 °F | Procedure A, C.125; ASTM D4226 |
| J/cm @Temperature 23.0 °C | ft-lb/mil @Temperature 73.4 °F | Procedure B, C.125; ASTM D4226 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | µm/m-°C | µin/in-°F | ASTM D696 |
| 载荷下热变形温度(0.46 MPa) | °C @Treatment Temp. 60.0 °C | °F @Treatment Temp. 140 °F | Annealed; ASTM D648 |
| °C @Treatment Temp. 50.0 °C, Thickness 3.18 mm | °F @Treatment Temp. 122 °F, Thickness 0.125 in | Annealed; ASTM D648 | |
| 载荷下热变形温度(1.8 MPa) | °C @Treatment Temp. 60.0 °C | °F @Treatment Temp. 140 °F | Annealed; ASTM D648 |
| °C @Treatment Temp. 50.0 °C, Thickness 3.18 mm | °F @Treatment Temp. 122 °F, Thickness 0.125 in | Annealed; ASTM D648 | |
| 可燃性(UL94) | @Thickness 1.50 - 3.00 mm | @Thickness 0.0591 - 0.118 in | natural; UL 94 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | °C | °F |
| 材料描述 | 测试方法 | |
|---|---|---|
| 特性 | High Stiffness | |
| Low CLTE | ||
| 形式 | Cube | |
| 通用材料 | PVC, Rigid | |
| 通用名 | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| 加工方法 | Extrusion | |
| PVC Cell Classification | 12474 | ASTM D1784 |
| 供货地区 | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| 用途 | General Purpose | |
| Profiles |