High-strength and high-stiff parts; low coefficient of expansion.
Dynamic stressed parts at high movement velocity.
Chemical and hydrolysis resistance parts, non flammable.
Electrically conductive, suitable for continuous discharging of statically generated electricity.
Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.
Information provided by Lehmann & Voss & Co.KG| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | g/cc | g/cc | ISO 1183 |
| 吸水率 | 23°C/24h | ||
| 线性成型收缩率 | cm/cm | in/in | |
| 熔体流动速率 | g/10 min @Load 10.0 kg, Temperature 380 °C | g/10 min @Load 22.0 lb, Temperature 716 °F |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度 | MPa | psi | |
| 屈服伸长率 | |||
| flexural | |||
| 弹性模量 | GPa | ksi | |
| 弯曲强度 | MPa | psi | |
| 弯曲模量 | GPa | ksi | |
| 简支梁无缺口冲击强度 | J/cm² | ft-lb/in² | edgewise; ISO 179 1eU |
| 简支梁缺口冲击强度 | J/cm² | ft-lb/in² | ISO 179 1eA |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 表面电阻 | <= ohm | <= ohm | |
| 绝缘电阻 | <= ohm | <= ohm |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 最高工作温度, Air | °C | °F | |
| °C | °F | short term |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工温度 | °C | °F | mass temp |
| 射嘴温度 | °C | °F | |
| 1区 | °C | °F | |
| 2区 | °C | °F | |
| 3区 | °C | °F | |
| 模具温度 | °C | °F | |
| 干燥温度 | °C @Time 21600 - 28800 sec | °F @Time 6.00 - 8.00 hour | or |
| °C @Time 10800 - 21600 sec | °F @Time 3.00 - 6.00 hour | Dehumidifying dryer |
| 材料描述 | 测试方法 | |
|---|---|---|
| 颜色 | natural color (black) |