Information provided by LNP, a GE Plastics Company.
This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | g/cc | g/cc | Method A; ASTM D792 |
| 密度 | g/cc | lb/in³ | ISO 1183 |
| 线性成型收缩率 | cm/cm | in/in | ASTM D955 |
| 线性成型收缩率，横向 | cm/cm | in/in | ASTM D955 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | MPa | psi | ASTM D638 |
| 伸长率 (断裂) | ASTM D638 | ||
| 拉伸模量 | GPa | ksi | ASTM D638 |
| 弯曲强度 | MPa | psi | ASTM D790 |
| 弯曲模量 | GPa | ksi | ASTM D790 |
| 悬壁梁缺口冲击强度 | J/cm @Thickness 3.18 mm | ft-lb/in @Thickness 0.125 in | ASTM D256 |
| 悬壁梁无缺口冲击强度 | J/cm @Thickness 3.18 mm | ft-lb/in @Thickness 0.125 in | ASTM D256 |
| 悬壁梁缺口冲击强度 | kJ/m² | ft-lb/in² | ISO 180 |
| 悬壁梁无缺口冲击强度 | kJ/m² | ft-lb/in² | ISO 180 |
| Falling Dart Impact | J | ft-lb | ASTM D3763 |
| 冲击试验 | J | ft-lb | Multi-Axial Instrumented Impact Energy; ISO 6603-2 |
| 动态摩擦系数 | vs. Steel - @ 40 psi, 50 ft/min, tested in accordance with LNP WI-0687; ASTM D1894 | ||
| 静态摩擦系数 | vs. Steel @ 40 psi, tested in accordance with LNP WI-0687; ASTM D1894 | ||
| K (wear) Factor | x 10-8 mm³/N-M | x 10-10 in³-min/ft-lb-hr | 40psi, 50ft/min; tested in accordance with LNP WI-0687 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度(1.8 MPa) | °C | °F | Unannealed; ASTM D648 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | °C | °F | |
| 模具温度 | °C | °F | |
| 干燥温度 | °C | °F | |
| 干燥时间 | hour | hour | |
| 背压 | MPa | psi |
| 材料描述 | 测试方法 | |
|---|---|---|
| 颜色 | Black |