| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | ISO 1183 |
| 粘度测试 | cm³/g | cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| 熔体流动速率 | g/10 min @Load 5.00 kg, Temperature 270 °C | g/10 min @Load 11.0 lb, Temperature 518 °F | Estimated using room temperature density; ISO 1133 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | MPa | psi | Conditioned; ISO 527-1/-2 |
| MPa | psi | ISO 527-1/-2 | |
| 伸长率 (断裂) | ISO 527-1/-2 | ||
| Conditioned; ISO 527-1/-2 | |||
| 拉伸模量 | GPa | ksi | Conditioned; ISO 527-1/-2 |
| GPa | ksi | ISO 527-1/-2 | |
| 简支梁无缺口冲击强度 | J/cm² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU |
| J/cm² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | Conditioned; ISO 179/1eU | |
| J/cm² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |
| J/cm² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | Conditioned; ISO 179/1eU | |
| 简支梁缺口冲击强度 | J/cm² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA |
| J/cm² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |
| 多轴向仪器化冲击能量 | J | ft-lb | ISO 6603-2 |
| J | ft-lb | Conditioned; ISO 6603-2 | |
| J @Temperature -30.0 °C | ft-lb @Temperature -22.0 °F | ISO 6603-2 | |
| J @Temperature -30.0 °C | ft-lb @Temperature -22.0 °F | Conditioned; ISO 6603-2 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | ohm-cm | ohm-cm | Conditioned; IEC 60093 |
| ohm-cm | ohm-cm | IEC 60093 | |
| 表面电阻 | ohm | ohm | IEC 60093 |
| 介电常数 | @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | IEC 60250 |
| @Frequency 100 Hz | @Frequency 100 Hz | IEC 60250 | |
| @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | Conditioned; IEC 60250 | |
| @Frequency 100 Hz | @Frequency 100 Hz | Conditioned; IEC 60250 | |
| 耗散因数 | @Frequency 100 Hz | @Frequency 100 Hz | IEC 60250 |
| @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | IEC 60250 | |
| @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | Conditioned; IEC 60250 | |
| @Frequency 100 Hz | @Frequency 100 Hz | Conditioned; IEC 60250 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | µm/m-°C | µin/in-°F | ISO 11359-1/-2 |
| 线性热膨胀系数,横向流动 | µm/m-°C | µin/in-°F | ISO 11359-1/-2 |
| 熔融温度 | °C | °F | 10°C/min; ISO 11357-1/-3 |
| 载荷下热变形温度(0.46 MPa) | °C | °F | ISO 75-1/-2 |
| 载荷下热变形温度(1.8 MPa) | °C | °F | ISO 75-1/-2 |
| 载荷下热变形温度(8.0 MPa) | °C | °F | ISO 75-1/-2 |
| 可燃性(UL94) | @Thickness 0.800 mm | @Thickness 0.0315 in | IEC 60695-11-10 |
| @Thickness 1.60 mm | @Thickness 0.0630 in | IEC 60695-11-10 |
| 材料描述 | 测试方法 | |
|---|---|---|
| Additives | Release agent | |
| 特性 | Heat stabilized or stable to heat | |
| U.V. stabilized or stable to weather | ||
| 形式 | Pellets | |
| ISO Shortname | ISO 1874-PA 6,MHLR,14-070,GF20 | |
| 加工 | Injection molding | |
| 区域 | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |